The invention provides a self-adhesive sound insulation expansion adhesive, which consists of 100 parts of butyl rubber, 300-500 parts of calcium carbonate filler, 30-50 parts of processing oil, 70-100 parts of polyisobutylene, 10-30 parts of tackifying resin, 2-5 parts of antioxidant, 10-20 parts of carbon black, 10-15 parts of expansion beads and 2-4 parts of cobalt salt. The preparation method is as follows: after kneading butyl rubber and part of filler calcium carbonate in kneading machine for 10 minutes, adding polyisobutylene, antioxidant, carbon black, processing oil and remaining filler calcium carbonate, kneading for 30 minutes; adding tackifying resin and cobalt salt, kneading for 30 minutes; adding expanded microspheres, kneading for one hour; extruding through a screw Extruding, calendering and laminating, the self adhesive type expansion rubber is obtained. It has good initial adhesion when contacting with other parts, and can maintain excellent adhesion at high temperature without crosslinking.
【技术实现步骤摘要】
一种自粘型隔音膨胀胶及其制备方法
本专利技术属于膨胀胶
，具体涉及一种自粘型隔音膨胀胶及其制备方法。
技术介绍
传统的汽车用隔音膨胀胶大多采用EPDM(三元乙丙橡胶)作为主体，加入各种助剂、填料、交联剂，通过密炼、成型而成，在使用过程需要通过胶黏剂或者粘结层与汽车部件结合。现有技术具有以下缺陷和不足：1.目前的隔音膨胀胶和汽车部件粘结主要依靠胶黏剂，首先，胶黏剂成本较高，同时在生产过程中增加了数道生产工序，增加了加工成本和作业难度；其次，使用过程中可能产生胶黏剂与膨胀胶的结合失效问题，降低了使用安全性。2.膨胀胶生产过程中增加粘结层也可以起到粘结效果，但是两者配方差异较大，生产设备不同，大大增加了同时生产的难度和成本，在使用过程中也容易产生粘结层和膨胀胶脱落的问题。
技术实现思路
本专利技术的目的是提供一种工艺简单、产品失效风险低的自粘型隔音膨胀胶，以解决隔音膨胀胶和汽车部件的粘接问题。本专利技术提供了如下的技术方案：本专利技术的自粘型隔音膨胀胶按重量份的组成为：丁基橡胶100份填料碳酸钙300～500份加工油30～50份聚异丁烯70～100份增粘树脂10～30...
【技术保护点】
1.一种自粘型隔音膨胀胶，其特征在于，所述自粘型隔音膨胀胶按重量份的组成为：
【技术特征摘要】
1.一种自粘型隔音膨胀胶，其特征在于，所述自粘型隔音膨胀胶按重量份的组成为：2.根据权利要求1所述的自粘型隔音膨胀胶，其特征在于，所述加工油为环烷基油或者石蜡基油。3.根据权利要求1所述的自粘型隔音膨胀胶，其特征在于，所述增粘树脂为C5石油树脂或者萜烯树脂或者203树脂或者癸酸钴树脂。4.根据权利要求1所述的自粘型隔音膨胀胶，其特征在于，所述防老剂为N-苯基-β-萘胺。5.根据权利要求1所述的自粘型隔音膨胀胶，其特征在于，所述膨胀微珠为MSH-...
【专利技术属性】
技术研发人员：周毕萌，王金艳，姚三川，
申请(专利权)人：江苏同盟汽车零部件实业有限公司，
类型：发明
国别省市：江苏,32