The invention provides a compound agent for efficiently removing cadmium from cyanide cadmium plating wastewater and a preparation method thereof, belonging to the technical field of environmental protection. The utility model solves the problem of poor effect of waste water treatment in the prior art. The cadmium ion compound agent for high efficiency removal of wastewater includes composite aluminum iron, calcium chloride, trisodium phosphate, activated attapulgite and a small amount of polyacrylic acid. The preparation method of the compound agent for efficiently removing cadmium from cyanide cadmium plating wastewater comprises the following steps: A, preparation; B, preliminary mixing; C, subsequent mixing; D, packaging. The composite wastewater from cyanide cadmium plating wastewater is highly effective.
【技术实现步骤摘要】
高效去除有氰镀镉废水中镉的复合剂及其制备方法
本专利技术属于环保
，涉及一种高效去除有氰镀镉废水中镉的复合剂及其制备方法。
技术介绍
镉为稀有元素，符号Cd，呈银白色，熔点320.9℃。镉是作为副产品从锌矿石或硫镉矿中提炼出来的，大多用来保护其他金属免受腐蚀和锈损，如电镀钢、铁制品、铜、黄铜及其他合金。镉是高危害有毒物质和可致癌物质，不是人体的必需元素，被镉污染的水体、空气、土壤和食物对人体危害严重，且在人体内代谢较慢，日本因镉中毒曾出现“痛痛病”。在我国被列为一类污染物，重点监控，环太湖流域的排放指标为≤0.01PPM(或10PPB)，即，GB21900-2008表3排放标准。含Cd废水处理的常见方法主要有沉淀法(氢氧化物或硫化物沉淀法)、离子树脂交换法、电解法、吸附法及反渗透法等，这些方法虽对Cd有一定的去除效果，但均存在处理成本高及处理效果不好(很难稳定到达≤0.01PPM排放指标)等缺点。
技术实现思路
本专利技术的第一个的目的是针对现有技术存在的上述问题，提供一种含镉废水处理效果好的高效去除有氰镀镉废水中镉的复合剂。本专利技术的第二个目的是提供上述高效...
【技术保护点】
1.一种高效去除废水中镉离子复合剂，其特征在于，包含复合铝铁，氯化钙、磷酸三钠，活化凹凸棒及少量聚丙烯酸，所述的复合剂质量百分比如下：复合铝铁：30‑60％氯化钙：5‑25％磷酸三钠：20‑50％活化凹凸棒：15‑25％聚丙烯酸：0.2‑0.6％。
【技术特征摘要】
1.一种高效去除废水中镉离子复合剂，其特征在于，包含复合铝铁，氯化钙、磷酸三钠，活化凹凸棒及少量聚丙烯酸，所述的复合剂质量百分比如下：复合铝铁：30-60％氯化钙：5-25％磷酸三钠：20-50％活化凹凸棒：15-25％聚丙烯酸：0.2-0.6％。2.根据权利要求1所述的高效去除废水中镉离子复合剂，其特征在于，所述复合剂的优选质量百分比为：复合铝铁：50-60％氯化钙：10-20％磷酸三钠：25-35％活化凹凸棒：15-20％聚丙烯酸：0.2-0.6％。3.根据权利要求1或2所述的高效去除废水中镉离子复合剂，其...
【专利技术属性】
技术研发人员：周健，胡国辉，杨关义，
申请(专利权)人：嘉兴通惠环保科技有限公司，
类型：发明
国别省市：浙江,33