The invention discloses a preparation method of activated carbon loaded manganese dioxide, the steps are as follows: the activated carbon is cleaned with deionized water, and the surface impurities are removed, and the activated carbon is dried at 75 85 C for 4 6 h to constant weight; The treated activated carbon is placed in Mn (NO3) 2 solution of 0.4 mol/L and Na2CO3 solution of 0.5 mol/L respectively. After shaking for 6 7 h, soaking, washing, drying at 60 70 C, calcining in a muffle furnace at 330 350 C for 4 6 h, cooling is available. The method is simple, rapid and easy to operate. The adsorption sites on the surface of the catalyst are increased, the interaction between the catalyst and Rhodamine B is strengthened, and the decolorization performance is enhanced.
【技术实现步骤摘要】
一种活性炭负载二氧化锰的制备方法
本专利技术涉及一种活性炭负载二氧化锰的制备方法。
技术介绍
印染废水成分复杂、排放量大，不但影响外观，阻碍光线渗透和扰乱生物生命过程，而且对人类眼睛、皮肤等有危害，一直是污水处理中的难题。调查表明，全世界每年生产的染料超70万t，其中2%直接以废水的形式排出，10%在随后的纺织染色过程中损失。罗丹明B（花粉红）是一种具有鲜桃红色的人工合成染料，被广泛用作织物、皮革、生物染色等方面，其废水色度高、难降解等特点，被怀疑是致癌物质。染料废水处理可采用混凝沉淀、化学氧化法、电化学法等，但存在工艺复杂，污泥量大等问题。吸附法是处理印染废水有效处理方法之一。近年来，许多学者研究活性炭上负载金属离子，改变活性炭表面性能，以达到更佳的处理效果。MnO2是一种新型的水处理负载材料，其比表面积大、粒径小、吸附、氧化及催化性能高，对水中重金属离子、苯酚、有机染料废水等均有具有较强的去除能力。有关MnO2的负载制备方法主要有氧化还原法、溶胶-凝胶法、水热法以及高温分解等。碳酸锰热分解法因为原料易得，工艺条件易控制、生产成本低而得以广泛应用。尽管关于MnO...
【技术保护点】
1.一种活性炭负载二氧化锰的制备方法，其特征在于包括如下步骤：将活性炭用去离子水清净，去除表面杂质，75‑85℃下恒温烘干4‑6h至恒重；将25‑35份上述处理过的活性炭分别依次置于65‑75份浓度为0.4mol/L的Mn(NO3)2和60‑70份浓度为0.5mol/L的Na2CO3溶液中，摇床振荡6‑7h，浸渍，冲洗，60‑70℃干燥后，置于马弗炉中于330‑350℃煅烧4‑6h，冷却即得；各原料均为重量份。
【技术特征摘要】
1.一种活性炭负载二氧化锰的制备方法，其特征在于包括如下步骤：将活性炭用去离子水清净，去除表面杂质，75-85℃下恒温烘干4-6h至恒重；将25-35份上述处理过的活性炭分别依次置于65-75份浓度为0.4mol/L的Mn(NO3)2和60-70份浓度为0.5mol/L的Na2CO3溶液中，摇床振荡6-7h，浸渍，冲洗，60-70℃干燥后，...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：启东祥瑞建设有限公司，
类型：发明
国别省市：江苏,32