一种可作为涂层添加剂的碳纳米颗粒及其制备方法和应用技术
Carbon nano particle capable of being used as coating additive and preparation method and application thereof
The invention discloses a carbon nanoparticle which can be used as coating additive, its preparation method and application, and can prepare high purity, high yield and uniform particle size carbon nanoparticles simply and quickly. Moreover, the carbon nanoparticle of the invention has good biocompatibility, non-toxicity and biodegradability, and the carbon nanoparticle can be biodegraded. As a coating additive, the cost of carbon nanoparticles per gram is only 0.7 yuan, and the amount of carbon nanoparticles per liter of coating is only 5 g. Therefore, the cost is low. The most important thing is that the carbon nanoparticles can meet the dual functional requirements of biological anti-fouling and anti-corrosion through strong negative potential effect on the surface.
【技术实现步骤摘要】
一种可作为涂层添加剂的碳纳米颗粒及其制备方法和应用
本专利技术属于高分子发光材料
，具体涉及一种可作为涂层添加剂的碳纳米颗粒及其制备方法和应用。
技术介绍
海洋约占地球表面积的70%，丰富的海洋资源对于人类社会发展起到了至关重要的作用，人类为了获取海洋资源而大力发展船舶业。由于船舶制造常用到铁等金属材料，而海洋环境对铁等金属材料易造成严重的腐蚀，这给船舶制造业的发展带来了极大的挑战。海水的成分极其复杂，几乎含有地球上所有化学元素的化合物，并且还含有大量的溶解氧、海洋生物和腐败有机物等，这些物质对于金属构件造成了巨大的危害。此外，波浪、潮汐对金属构件所产生低频往复应力和冲击加速了腐蚀的过程。我国每年由于腐蚀造成的损失约为GDP的5％，国际上公认腐蚀损失超过所有自然灾害损失的总和。在海洋环境中服役的基础设施和重要工业设施的腐蚀问题严重，特别是船舶与海洋平台的腐蚀问题更加突出，腐蚀已经成为影响船舶、近海工程、远洋设施服役安全、寿命、可靠性的最重要因素，引起世界各国政府和工业界的高度重视。海洋生物种类繁多，海洋生物在船舶等设备上附着会加速金属腐蚀，增加燃油损耗，增大...
【技术保护点】
1.一种可作为涂层添加剂的碳纳米颗粒，其特征在于：所述碳纳米颗粒的尺寸为3‑5nm，晶格间距为0.21 nm，对应石墨碳的（100）晶面，所述碳纳米颗粒的表面上具有多个含氧官能团。
【技术特征摘要】
1.一种可作为涂层添加剂的碳纳米颗粒，其特征在于：所述碳纳米颗粒的尺寸为3-5nm，晶格间距为0.21nm，对应石墨碳的（100）晶面，所述碳纳米颗粒的表面上具有多个含氧官能团。2.根据权利要求1所述的可作为涂层添加剂的碳纳米颗粒，其特征在于：所述含氧官能团为-OH、-COOH和C-O-C中的任意一种或几种。3.一种可作为涂层添加剂的碳纳米颗粒的制备方法，其特征在于，该方法包括如下步骤：（1）取两根石墨棒用超纯水超声清洗，将洗净的两根石墨棒备用；（2）将两根石墨棒均置于电解液中，两根石墨棒之间保持间距；（3）在两根石墨棒之间施加恒定的电流，并持续电解至电解液变成深棕色；（4）将深棕色的电解液过滤，采用透析法去除可溶性杂质后，获得可作为涂层添加剂的碳纳米颗粒。4.根据权利要求3所述的可作为涂层添加剂的碳纳米颗粒的制备方法，其特征在于：步...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。