The invention discloses an environment-friendly multifunctional treatment agent, which is characterized in that it comprises the following raw materials according to the mass percentage: 30_50% phosphoric acid, 5_10% zinc oxide, 2_6% surfactant, 10_15% emulsifier, 0.2_0.5% potassium chlorate and 30_40% water. The present invention has many functions such as oil removal, rust removal, phosphating and ceramics. The oil removal, rust removal, phosphating and ceramics are completed at one time, the film is formed quickly, the adhesion between the substrate and the coating is good, and the corrosion resistance is good. It is widely used in various carbon steel, cast iron, pure iron, tool steel, alloy steel, alloy aluminum, cast aluminum and so on. It does not contain toxic and harmful substances. No waste water is discharged after the treatment, and the operation is simple.
【技术实现步骤摘要】
一种环保型多功能处理剂及其制备方法
本专利技术涉及表面处理剂领域，具体涉及一种环保型多功能处理剂及其制备方法。
技术介绍
钢铁制品在加工涂漆前要对其表面进行除油、除锈、磷化、陶化处理，使其生成转化膜，以防止中间过程的腐蚀，改善涂漆质量、延长钢铁的使用寿命。但是现有的磷化处理所用的处理剂大多数含有对人体及环境有害的成分，酸雾的蒸发、污水的排放都会对自然环境造成污染，而且工艺复杂、处理时间长、劳动强度大，且所用处理剂的配方多，配制繁琐，处理成本高。另一方面，不同金属工件进行综合处理化成处理时通常需要不同的处理剂，种类繁多难于管理和操作。
技术实现思路
：本专利技术的目的在于克服现有技术的不足，提供了一种环保型多功能处理剂及其制备方法。本专利技术采用以下技术方案：一种环保型多功能处理剂，其特征在于，按质量百分比计，包括如下原料：30-50％磷酸、5-10％氧化锌、2-6％表面活性剂、10-15％乳化剂、0.2-0.5％氯酸钾、30-40％水。优选地，按质量百分比计，包括如下原料：40％磷酸、8％氧化锌、4％表面活性剂、13％乳化剂、0.4％氯酸钾、34.6％水。优选地，所述...
【技术保护点】
1.一种环保型多功能处理剂，其特征在于，按质量百分比计，包括如下原料：30‑50％磷酸、5‑10％氧化锌、2‑6％表面活性剂、10‑15％乳化剂、0.2‑0.5％氯酸钾、30‑40％水。
【技术特征摘要】
1.一种环保型多功能处理剂，其特征在于，按质量百分比计，包括如下原料：30-50％磷酸、5-10％氧化锌、2-6％表面活性剂、10-15％乳化剂、0.2-0.5％氯酸钾、30-40％水。2.根据权利要求1所述的一种环保型多功能处理剂，其特征在于，按质量百分比计，包括如下原料：40％磷酸、8％氧化锌、4％表面活性剂、13％乳化剂、0.4％氯酸钾、34.6％水。3.根据权利要求1所述的一种环保型多功能处理剂，其特征在于，所述的表面活性剂为SC01，购于德国汉姆公司。4.根据权利要求1所述的一种环保型多功能处理剂，其特征在于，所述的乳化剂为OP-10，购于德国汉姆公司。5.根据权利要求1或2所述的一种环保型多功能处理剂，其特征在于，所述的表面活性剂为十二烷基硫酸钠、十二烷基苯磺酸钠、聚乙烯吡咯烷酮中的一种或多种组合。6....
【专利技术属性】
技术研发人员：梁少荣，
申请(专利权)人：中山市汇宏环保科技有限公司，
类型：发明
国别省市：广东,44