The invention discloses a manufacturing method of humic acid industrial briquette binder. The existing manufacturing methods of industrial briquette binders are divided into organic and inorganic types. Their disadvantages are that briquettes have low cold and heat strength, large ash content, low ash solubility and much reduction of fixed carbon. The method is accomplished by adding 450 550 phr of water and 150 250 phr of humic acid raw materials into a reaction kettle by weight, heating to 85 95 C, adding 60 90 phr of 30% caustic soda under stirring, adding 25 35 phr of formaldehyde and 5 15 phr of urea for 20 40 minutes, and then cooling to 40 50 minutes after reaction. Finished products. Compared with the existing technology, the coal ball made of the industrial briquette binder produced by the invention can remarkably improve the strength, ash solution point and gas emission, and basically does not reduce the fixed carbon.
【技术实现步骤摘要】
一种腐植酸工业型煤粘合剂的制造方法
本专利技术涉及一种工业型煤粘合剂的制造方法，特别涉及一种腐植酸工业型煤粘合剂的制造方法。
技术介绍
现有工业型煤粘合剂的制造方法分为有机型和无机型。有机型可用腐殖酸和糠醛渣在100℃时，加上一定比例的烧碱，制成腐钠，然后加入白煤沫中，压制成型。无机型是在成型前加入一定比例的石灰，成型后碳化，或成型前加入水泥、水玻璃等，成型后冷固化。上述方法的缺点在于，型煤成型后冷、热强度低，灰分大、灰溶点低，固定碳下降多，从而影响发气量，降低化肥产量。
技术实现思路
本专利技术的目的在于克服上述缺点，提供一种工艺简单，造价低，性能优良的工业型煤粘合剂的制造方法。本专利技术的任务是这样完成的，以重量份计，将450-550份水、150-250份腐植酸原料加入反应釜中，加热至85-95℃，搅拌下加入60-90份30％的烧碱，反应20-40分钟后，加入25-35份甲醛、5-15份尿素，再反应30-50分钟后冷却至40℃，即为成品。利用本专利技术生产的工业型煤粘合剂制成的煤球，与现有技术相比，可显著提高强度，灰溶点、发气量，基本不降低固定碳。具体实施方式施实例首先将500㎏水、200㎏腐植酸原料加入反应釜中，加热至90℃，搅拌下加入80㎏30％的烧碱，反应30分钟后，加入30㎏甲醛、10㎏尿素，再反应40分钟后冷却至40℃，即为成品。
【技术保护点】
1.一种腐植酸工业型煤粘合剂的制造方法，其特征在于，它是以重量份计，将450‑550份水、150‑250份腐植酸原料加入反应釜中，加热至85‑95℃，搅拌下加入60‑90份30％的烧碱，反应20‑40分钟后，加入25‑35份甲醛、5‑15份尿素，再反应30‑50分钟后冷却至40℃，即为成品。
【技术特征摘要】
1.一种腐植酸工业型煤粘合剂的制造方法，其特征在于，它是以重量份计，将450-550份水、150-250份腐植酸原料加入反应釜中，加热至85-95...
【专利技术属性】
技术研发人员：刘文陟，
申请(专利权)人：韩城市旺源再生燃料有限责任公司，
类型：发明
国别省市：陕西,61