一种由煤泥加工而成的型煤制造技术

本发明专利技术涉及一种由煤泥加工而成的型煤。它以脱水煤泥为主要原料，加入脱水煤泥重量0.5‑15％的废碱泥，2‑8％的锯末，0.5‑5％的废塑料膜，0‑2％的碎麻刀搅拌制成。与同质煤泥相比其燃烧性能有明显改善。表现为易燃、烟小、燃烧速度均匀，非燃烧性损耗小，利用率高，而且其强度接近原生块煤水平，运输方便，对环境污染小。

A briquette made from coal slime

The invention relates to a briquette made from coal slime. It is made of dehydrated coal slime as the main raw material, adding the waste alkali slime with the weight of dehydrated coal slime of 0.5 15%, sawdust with the weight of 2 8%, plastic film with the waste of 0.5 5% and hemp knife with the size of 0 2%. Compared with homogenous slime, its combustion performance has been improved significantly. It is characterized by flammability, small smoke, uniform combustion speed, low Non-combustibility loss, high utilization rate, and its strength is close to the level of primary lump coal, convenient transportation, and less pollution to the environment.

【技术实现步骤摘要】
一种由煤泥加工而成的型煤
本专利技术涉及一种型煤，具体地说是一种由煤泥加工而成的型煤。
技术介绍
目前较大煤矿几乎都有洗煤设备，而洗选原煤的废水中都带有大量的煤泥，由于其燃烧性差，又难于运输，绝大部分随废水排出，不仅造成了极大的浪费，而且又给周围环境造成了严重的污染。
技术实现思路
本专利技术的目的在于提供一种不仅强度高，而且燃烧性能好的以洗选原煤过程中产生的废煤泥制作的型煤。本专利技术的任务是这样完成的，将煤泥中的水分脱水到15％以下，加入煤泥重量0.5-15％的废碱泥，2-8％的锯末，0.5-5％的废塑料膜，0-2％的碎麻刀，搅拌后可根据其用途制成任意形状的型煤直接装箱。本专利技术的优点是：在燃烧时，由于碱泥的燃烧催化作用，锯末和塑料膜的引燃作用，其燃烧性能与同质煤泥相比有明显改善。表现为易燃、烟小、燃烧速度均匀，非燃烧性损耗小，利用率高。其强度接近原生块煤水平，运输方便，对环境污染小。具体实施方式施实例称取脱水煤泥800千克，废碱泥80千克，干锯末40千克，粉碎到3-5毫米的碎麻刀8千克，粉碎到4平方毫米以下的废塑料膜30千克，充分搅拌后成型即可。

【技术保护点】
1.一种由煤泥加工而成的型煤，其特征在于，它以脱水煤泥为主要原料，添加煤泥重量0.5‑15％的废碱泥，2‑8％的锯末，0.5‑5％的废塑料膜，0‑2％的碎麻刀搅拌制成。

【技术特征摘要】
1.一种由煤泥加工而成的型煤，其特征在于，它以脱水煤泥为主要原料，添加煤泥重量0.5...

【专利技术属性】
技术研发人员：刘文陟，
申请(专利权)人：韩城市旺源再生燃料有限责任公司，
类型：发明
国别省市：陕西,61