The invention discloses a scratch resistant PP plastic and a preparation method and application thereof. The scratch resistant PP plastic includes the following weight parts: PP plastic 68, 85, acrylic emulsion 20, 30, scratch resistant additive 0.2, 0.6, coupling agent 1, 2, and the scratch proof additive includes the following weight ingredients: erucic amide 32, 45, benzo three azole, three, 1,4, cyclohexane, methanol, etc. 2, 17, zinc acetate 5, 15, coupling agent boric acid coupling agent. The scratch resistant PP plastic has excellent scratch resistance, excellent mechanical properties and excellent yellowing resistance, and can be used in the field of automotive interior accessories.
【技术实现步骤摘要】
一种耐划伤PP塑料及其制备方法和应用
本专利技术涉及一种塑料，具体是一种耐划伤PP塑料及其制备方法和应用。
技术介绍
PP塑料又称聚丙烯(Polypropylene，简称PP)，其具有较高的耐冲击性，机械性质强韧，抗多种有机溶剂和酸碱腐蚀。在工业界有广泛的应用，是常见的高分子材料之一。聚丙烯的结晶度高，结构规整，因而具有优良的力学性能，但在塑料材料中仍属于偏低的品种，其拉伸强度仅可达到30MPa或稍高的水平。虽然聚丙烯具有良好的电性能和高频绝缘性且不受湿度影响，但其耐划伤性能差，导致PP塑料的应用范围受限。因此，本专利技术提供一种耐划伤PP塑料及其制备方法和应用。
技术实现思路
本专利技术的目的在于提供一种耐划伤PP塑料及其制备方法和应用，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种耐划伤PP塑料，所述耐划伤PP塑料包括以下重量份数的原料：PP塑料68-85份、丙烯酸乳液20-30份、耐划伤添加剂0.2-0.6份、偶联剂1-2份；所述耐划伤添加剂包括以下重量份数的原料：芥酸酰胺32-45份、苯并三氮唑13-20份、1,4-环己烷二甲...
【技术保护点】
1.一种耐划伤PP塑料，其特征在于，所述耐划伤PP塑料包括以下重量份数的原料：PP塑料68‑85份、丙烯酸乳液20‑30份、耐划伤添加剂0.2‑0.6份、偶联剂1‑2份；所述耐划伤添加剂包括以下重量份数的原料：芥酸酰胺32‑45份、苯并三氮唑13‑20份、1,4‑环己烷二甲醇12‑17份、醋酸锌5‑15份；偶联剂采用硼酸酯偶联剂。
【技术特征摘要】
1.一种耐划伤PP塑料，其特征在于，所述耐划伤PP塑料包括以下重量份数的原料：PP塑料68-85份、丙烯酸乳液20-30份、耐划伤添加剂0.2-0.6份、偶联剂1-2份；所述耐划伤添加剂包括以下重量份数的原料：芥酸酰胺32-45份、苯并三氮唑13-20份、1,4-环己烷二甲醇12-17份、醋酸锌5-15份；偶联剂采用硼酸酯偶联剂。2.根据权利要求1所述的耐划伤PP塑料，其特征在于，所述耐划伤PP塑料包括以下重量份数的原料：PP塑料72-80份、丙烯酸乳液23-28份、耐划伤添加剂0.3-0.5份、偶联剂1.2-1.8份；所述耐划伤添加剂包括以下重量份数的原料：芥酸酰胺35-40份、苯并三氮唑15-17份、1,4-环己烷二甲醇13-15份、醋酸锌8-12份。3.根据权利要求1所述的耐划伤PP塑料，其特征在于，所述耐划伤PP塑料包括以下重量份数的原料：PP塑料75份、丙烯酸乳液25份、耐划伤添加剂0.4份、偶联剂1.5份；所述耐划伤添加剂包括以下重量份数的原料：芥酸酰胺37份、苯并三氮唑16份、1,4-环己烷二甲醇14份、醋酸锌10份。4.一种如权利要求1-3任一所述的耐划伤PP塑料的制备方法，其特征在于，包...
【专利技术属性】
技术研发人员：宋啸萌，
申请(专利权)人：苏州睿烁环境科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。