本发明专利技术涉及一种塑料制作方法，包括以下步骤：取三醋酸纤维素50—70份，柠檬酸三丁酯30—40份，抗氧化剂20—30份，按照一定的比例混合起来，并经过搅拌得到混合物；将上述得到的混合物放在水浴锅中加热2—7小时，并设定加热温度为70℃—110℃；将加热得到的混合物在塑料成型机上加工成型。本发明专利技术的制作原料环保且成本低廉，制作而成的塑料坚固耐用，着色均匀，且增速性强，本发明专利技术中的塑料的制作方法可在塑料制作领域广泛推广。

Method for making plastics

The invention relates to a method for making plastics, which comprises the following steps: taking 50-70 parts of cellulose triacetate, 30-40 parts of tributyl citrate and 20-30 parts of antioxidants, mixing them in a certain proportion, and stirring them to obtain a mixture; heating the mixture in a water bath pot for 2-7 hours, and setting the addition time. The heat temperature is 70 - 110 C, and the heated mixture is processed on the plastic forming machine. The prepared plastic has the advantages of environmental protection and low cost, strong durability, uniform coloring and strong speed-up. The method of making the plastic in the invention can be widely popularized in the field of plastic production.

【技术实现步骤摘要】
一种塑料制作方法
本专利技术涉及塑料制作
，具体是指一种塑料制作方法。
技术介绍
目前，利用塑料制作而成的板材在各种行业中均有应用，例如各种旅行用水杯、家具家电的外壳、电脑键盘等的制作中年均有所体现，而现有的塑料板材均是由几种混合物混合加工，并在一定的条件下加工而成的，其最主要的成分是高分子聚合物或者合成树脂，在实际的加工过程中，为了达到不同的功效，在混合物中还加入了各种添加剂，比如润滑剂、稳定剂、着色剂等。但是，在塑料的整个生产过程中，往往需要添加邻苯二甲酸酯类等物质作为增塑剂，此类增塑剂对人体有害无益，而增塑剂也很难被循环再利用，而且降解起来难度很大，这就使得塑料在使用完后丢掉时严重污染了环境，这就在很大程度上影响了塑料的生产和应用。
技术实现思路
为解决上述技术问题，本专利技术提供的技术方案为：一种塑料制作方法，包括以下步骤：(1)取三醋酸纤维素50—70份，柠檬酸三丁酯30—40份，抗氧化剂20—30份，按照一定的比例混合起来，并经过搅拌得到混合物；(2)将步骤(1)中得到的混合物放在水浴锅中加热2—7小时，并设定加热温度为70℃—110℃；(3)将步骤(2)中加热得到的混本文档来自技高网...

【技术保护点】
1.一种塑料制作方法，其特征在于，包括以下步骤：(1)取三醋酸纤维素50—70份，柠檬酸三丁酯30—40份，抗氧化剂20—30份，按照一定的比例混合起来，并经过搅拌得到混合物；(2)将步骤(1)中得到的混合物放在水浴锅中加热2—7小时，并设定加热温度为70℃—110℃；(3)将步骤(2)中加热得到的混合物在塑料成型机上加工成型。

【技术特征摘要】
1.一种塑料制作方法，其特征在于，包括以下步骤：(1)取三醋酸纤维素50—70份，柠檬酸三丁酯30—40份，抗氧化剂20—30份，按照一定的比例混合起来，并经过搅拌得到混合物；(2)将步骤(1)中得到的混合物放在水浴锅中加热2—7小时，并设定加热温度为70℃—110℃；(3)将步骤(2)中加热得到的混合物在塑料成型机上加工成型。2.根据权利要求1所述的一种塑料制作方法，...