The invention discloses a ceramic corundum abrasive, which is characterized in that the abrasive consists of 45_80 parts kyanite, 20_38 parts aluminium hydroxide, 5_17 parts high alumina cement, 2_8 parts sodium fluoride, 15_40 parts cryolite, 20_42 parts rutile titanium dioxide, 5_14 parts talc powder, 10_24 parts hydrophobic perlite, boron. Zinc acid is 0.5, 11, cobalt oxide 3, 4, water-soluble resin emulsion 10, 17, sodium silicate 3, 7, sodium borate 5, 11, chromium oxide 3, 3, and fly ash. The invention can effectively control the grain size according to the change of sintering temperature to meet the requirements of different particle size corundum abrasives in practical application, and improves the compressive strength of single particle corundum abrasives and further optimizes the internal microstructure compared with the prior art.
【技术实现步骤摘要】
一种陶瓷刚玉磨料
本专利技术涉及一种陶瓷刚玉磨料。
技术介绍
磨料在工业应用中有着不可替代的作用,伴随着工业和科学技术的不断进步,磨料的使用范围越来越大,对其性能要求也逐渐提高。陶瓷刚玉磨料是用溶胶-凝胶法制备的,因此可以使磨料达到化学组分上的均匀性,同时用烧结工艺取代了熔融制备工艺,使得该磨料是一种陶瓷化的多晶烧结体,可以使磨料的硬度和韧性等大幅度提高。用溶胶-凝胶这种湿化学方法制备出来的陶瓷刚玉磨料在显微结构、磨削性能、韧性等许多方面表现优于传统熔融刚玉磨料;在制备成磨具使用时,也表现出良好的综合性能,陶瓷刚玉磨料的磨粒锋利,切削性能好,磨削效率高,可以进行大切深、大进给和高效磨削;自锐性好,能够不断暴露出新的切削面,使砂轮保持磨削稳定性;价格远低于CBN和金刚石等高档次磨料;磨具通用性好;功耗低,发热量少,不易烧伤工件;磨具耐用性好,可大量减少非磨削加工时间,大大提高其使用效率。然而,由于纯氧化铝的烧结扩散活化能较高,低温下难以烧结,过高温度又易引起晶粒的异常生长,孔隙率提高,破坏其微观结构的均一性、致密性,进而损坏其性能,因此,如何通过优化以提高其显微结构的性能一直是陶瓷刚玉磨料研究的重要内容。
技术实现思路
本专利技术所要解决的技术问题是提供一种高抗压强度的陶瓷刚玉磨料。为解决上述技术问题,本专利技术采用的技术方案是:一种高抗压强度的陶瓷刚玉磨料,其特征在于,包括下列重量份数的物质:蓝晶石45-80份,氢氧化铝20-38份,高铝水泥5-17份,氟化纳2-8份,冰晶石15-40份,金红石型钛白粉20-42份,滑石粉5-14份,憎水珍珠岩10-24份,硼 ...
【技术保护点】
1.一种陶瓷刚玉磨料,其特征在于,包括下列重量份数的物质:蓝晶石45‑80份,氢氧化铝20‑38份,高铝水泥5‑17份,氟化纳2‑8份,冰晶石15‑40份,金红石型钛白粉20‑42份,滑石粉5‑14份,憎水珍珠岩10‑24份,硼酸锌0.5‑11份,氧化钴3‑4份,水溶性树脂乳液10‑17份,硅酸钠3‑7份,硼酸钠5‑11份,氧化铬3‑9份,粉煤灰35‑46份。
【技术特征摘要】
1.一种陶瓷刚玉磨料,其特征在于,包括下列重量份数的物质:蓝晶石45-80份,氢氧化铝20-38份,高铝水泥5-17份,氟化纳2-8份,冰晶石15-40份,金红石型钛白粉20-42...