The invention discloses a cement sand clay surfactant. The raw material comprises the following components. The weight ratio of each component is 50-60 phr of hydrogenated rosin, 15-20 phr of sodium silicate, 3-5 phr of hydroxypropyl cellulose (HPMC), 0.1-0.3 phr of polyaspartic acid and 70 phr of water. The surfactant prepared according to the above proportion has small dosage. It is stable in function, good for construction, high performance, low cost, strong diffusion of solution, and improves age strength and durability of concrete. It is not only suitable for road system application, but also can be made into various brick masonry, saving material and labor.
【技术实现步骤摘要】
一种水泥砂石粘土表面活性剂的配制及工艺
：本专利技术涉及一种水泥砂石粘土表面活性剂的配制及工艺，属混凝土添加剂类。
技术介绍
：要致富先修路，随着农村道路的升级改造，需要的建材越来越多，尤其是基础设施工程建设所需建材。人们迫切希望能就地取材，因地制宜，节省成本，使用一种表面活性剂能减少建材消耗，达到资源节约，环境友好，工程优质的目标。
技术实现思路
：本专利技术的目的，就在于减少水泥的基础上，还能保持混凝土的强度所需的一种水泥砂石粘土表面活性剂。本专利技术的目的是通过以下技术方案来实现：一种水泥砂石粘土表面活性剂的配制及工艺，其原料包括以下组分，各组分的重量比为：氢化松香50～60份；水玻璃15～20份；羟丙基纤维素(HPMC)3～5份；聚天冬氨酸0.1～0.3份，水70份。其配制工艺依上述配制比例将50～60份氢化松香粉碎至60目，分散于70～80℃的50份水中，加入15～20份水玻璃，搅拌溶解乳化20分钟，停止加热至氢化松香乳液冷却至40℃以下时，将3～5份羟丙基纤维(HPMC)溶于20份水中的溶液，加入其中，搅拌均匀，冷至常温再加入聚天冬氨酸0.1～0.3份，搅拌5分钟即可。本专利技术具有以下优点：1、具有掺量小，功能稳定，引气量适中，泡沫稳定，利于提高混凝土施工和易性。2、高性能，低成本，溶液扩散力强，使混凝土更加密实，从而提高凝土的龄期强度和耐久性，不仅适于道路系统应用，还能制成各种砖块砌体，省料省工。具体实施方式：下面结合实施例，对本专利技术进一步描述。实例1：一种水泥砂石粘土表面活性剂配制氢化松香：52水玻璃：18羟丙基纤维素：3聚天冬氨酸：0....
【技术保护点】
1.一种水泥砂石粘土表面活性剂，其特征在于：其原料包括以下组份，且各组份的重量比为：氢化松香50～60份；水玻璃15～20份；羟丙基纤维素(HPMC)3～5份；聚天冬氨酸0.1～0.3份，水70份。
【技术特征摘要】
1.一种水泥砂石粘土表面活性剂，其特征在于：其原料包括以下组份，且各组份的重量比为：氢化松香50～60份；水玻璃15～20份；羟丙基纤维素(HPMC)3～5份；聚天冬氨酸0.1～0.3份，水70份。2.如权利要求1所述的一种水泥砂石粘土表面活性剂的配制工艺，其特征在于：依上述比例...