The invention relates to a preparation method of a corrosion-resistant and wear-resistant coating on the surface of rod parts, in particular to a method for preparing a sucker rod by ultra-high speed laser cladding technology. By selecting suitable metal powder, adjusting the position of powder convergence point and laser focus, and adjusting technological parameters, the invention can quickly and accurately produce a sucker rod with nickel-based corrosion-resistant and wear-resistant coating with good surface smoothness, small thickness and no defects, thus realizing ultra-high speed laser cladding and improving production efficiency. The purpose of saving production cost.
【技术实现步骤摘要】
一种用于制造抽油杆的方法
本专利技术涉及一种杆类部件表面耐磨耐腐蚀层的制备方法，具体涉及一种使用超高速率激光熔覆制备抽油杆的方法，属于表面处理
技术介绍
抽油杆适用于油田的采油，是抽油系统中的重要组成部分，起到连接抽油机和抽油泵并传递动力的作用。目前油田的开发已进入高含水期，采出液的矿化度高，井液中含有CO2、H2S、盐水等腐蚀介质。以优质碳素钢或合金钢为原材料生产的抽油杆在井液介质中服役过程中，由于化学腐蚀和电化学腐蚀的双重作用，导致抽油杆的严重腐蚀，进而造成油井故障。且由于抽油杆在运行中不可避免地要与油管发生摩擦，进一步加剧了抽油杆表面的损坏。根据矿场应用经验，抽油杆的损坏中由于腐蚀和磨损引起的损坏占80%以上。目前为止，相关研究人员针对腐蚀和磨损问题展开了许多研究，主要的耐腐蚀磨损的方法有三种：加入缓蚀剂、电镀和激光熔覆。（1）加入缓蚀剂。缓蚀剂可以在抽油杆表面形成有一种致密的保护膜，是抽油杆本体与腐蚀介质隔离开，达到保护抽油杆的目的，形成的保护膜对偏磨还能起到一定的防治作用。但缓蚀剂要根据腐蚀形式和腐蚀介质进行选择，而实际工况的腐蚀形式和腐蚀介质...
【技术保护点】
1.一种用于制造抽油杆的方法，其特征在于该抽油杆包括抽油杆基体和熔覆在该基体上的涂层，该方法的步骤包括：（1）对镍基粉末筛分及净化处理，获得符合要求的粉末后，然后经过烘干处理后真空封存，备用；（2）设定超高速率激光熔覆的工艺参数，具体工艺是：光斑直径为1～3mm，立柱表面线速度即熔覆速率为20～100m/min，每转进给量0.2～0.4mm，激光功率为900～1600W，送粉速率为5～25g/min；（3）将表面光洁无缺陷、直径小于成品直径0.2～0.6mm的抽油杆基体装夹在数控设备的回转机构上，并调整光斑（激光焦点）和粉斑（镍基粉末汇聚点）相对于抽油杆基体待熔覆面上方的位...
【技术特征摘要】
1.一种用于制造抽油杆的方法，其特征在于该抽油杆包括抽油杆基体和熔覆在该基体上的涂层，该方法的步骤包括：（1）对镍基粉末筛分及净化处理，获得符合要求的粉末后，然后经过烘干处理后真空封存，备用；（2）设定超高速率激光熔覆的工艺参数，具体工艺是：光斑直径为1～3mm，立柱表面线速度即熔覆速率为20～100m/min，每转进给量0.2～0.4mm，激光功率为900～1600W，送粉速率为5～25g/min；（3）将表面光洁无缺陷、直径小于成品直径0.2～0.6mm的抽油杆基体装夹在数控设备的回转机构上，并调整光斑（激光焦点）和粉斑（镍基粉末汇聚点）相对于抽油杆基体待熔覆面上方的位置，使得镍基粉末以液滴的形式滴入基体表面的熔池与基体结合；（4）采用同轴送粉超高速激光熔覆方法，使用步骤（2）所述的工艺将步骤（1）所得的镍基粉末熔覆到抽油杆基体表...