The invention provides a sucker rod made by ultra-high speed laser cladding. Ni based wear resistant and corrosion resistant coatings were prepared on the surface of sucker rod by ultra high speed laser cladding. The wear and corrosion resistance and service life of the sucker rod manufactured by this method exceed those of the electroplated sucker rod currently used in China, and overcome the problems of poor coating smoothness and low production efficiency caused by the traditional laser cladding method, and can carry out large-scale batch production.
【技术实现步骤摘要】
一种采用超高速率激光熔覆方法制造的抽油杆
本专利技术涉及一种采用激光熔覆方法制造的杆类零件，尤其涉及一种采用高速率激光熔覆方法制造的抽油杆，属于激光增材制造领域。
技术介绍
抽油杆适用于油田的采油，是抽油系统中的重要组成部分，起到连接抽油机和抽油泵并传递动力的作用。因此要求抽油杆具有足够的强度和使用寿命，保证采油工作的顺利进行。目前油田的开发已进入高含水期，采出液的矿化度高，井液中含有CO2、H2S、盐水等腐蚀介质。抽油杆以优质碳素钢或合金钢为原材料生产的抽油杆在井液介质中服役过程中，由于化学腐蚀和电化学腐蚀的双重作用，导致抽油杆的严重腐蚀，进而造成油井故障。且由于抽油杆在运行中不可避免地要与油管发生摩擦，进一步加剧了抽油杆表面的损坏。根据矿场应用经验，抽油杆的损坏中由于腐蚀和磨损引起的损坏占80%以上。为了防止抽油杆的腐蚀，通常采用添加缓蚀剂、电镀技术和激光熔覆技术。缓蚀剂可以在抽油杆表面形成有一种致密的保护膜，是抽油杆本体与腐蚀介质隔离开，达到保护抽油杆的目的，但缓蚀剂很难全方面对抽油杆进行保护且保护周期也太短。使用最为广泛的方法是电镀技术工艺简单成本低廉，但...
【技术保护点】
1.一种采用超高速率激光熔覆方法制造的抽油杆，其特征在于包括抽油杆基体和涂层，该涂层通过下述方法熔覆在抽油杆基体上：（1）选择镍基粉末并对粉末筛分处理，然后经过烘干处理后真空封存，备用；（2）将抽油杆基体固定在车床上，车削外圆至直径小于成品直径0.2～0.6mm，检查基体表面，确保表面光洁无缺陷；（3）将抽油杆基体装夹在激光熔覆设备的回转机构上，调整光斑（激光焦点）和粉斑（镍基粉末汇聚点）相对基体外表面待熔覆面上方的位置，并使得激光束大部分能量能量作用在了粉末材料上；（4）采用同轴送粉超高速激光熔覆方法，使用步骤（3）所设定的工艺将步骤（1）所得的镍基粉末熔覆到基体表面，得...
【技术特征摘要】
1.一种采用超高速率激光熔覆方法制造的抽油杆，其特征在于包括抽油杆基体和涂层，该涂层通过下述方法熔覆在抽油杆基体上：（1）选择镍基粉末并对粉末筛分处理，然后经过烘干处理后真空封存，备用；（2）将抽油杆基体固定在车床上，车削外圆至直径小于成品直径0.2～0.6mm，检查基体表面，确保表面光洁无缺陷；（3）将抽油杆基体装夹在激光熔覆设备的回转机构上，调整光斑（激光焦点）和粉斑（镍基粉末汇聚点）相对基体外表面待熔覆面上方的位置，并使得激光束大部分能量能量作用在了粉末材料上；（4）采用同轴送粉超高速激光熔覆方法，使用步骤（3）所设定的工艺将步骤（1）所得的镍基粉末熔覆到基体表面，得到厚度为0.15～0.45mm的涂层；（5）在不送粉条件下降低激光功率，保持其它工艺参数不变，对熔覆涂层进行激光重熔，得到表面平滑光亮、无凹坑和裂纹的涂层；（6）将带有熔覆涂层的抽油杆进行磨床精加工至成品尺寸。2.根据权利要...
【专利技术属性】
技术研发人员：王淼辉，申博文，范斌，梁金明，杜博睿，葛学元，
申请(专利权)人：北京机科国创轻量化科学研究院有限公司，
类型：发明
国别省市：北京,11