The invention relates to a manufacturing process of conveyor belt and a pre-heat-treated corrugated cardboard belt fabric conveyor belt, which comprises the following steps: step 1, pre-heat treatment: before yarn lamination and twisting, the yarn is heat-treated at ambient temperature 90 160 C, steam chamber pressure 2 MPa 4 mpa, steam chamber humidity greater than 90%, heat treatment 4. 5 min 60 min; Step 2, ply and twist: merge single strand yarn into single twist yarn; Step 3, fabric conveyor belt: warp and weft are woven into fabric conveyor belt. The conveyor belt produced by this process has many advantages, such as wear resistance, good adaptability, and accelerating moisture release.
【技术实现步骤摘要】
一种预先热处理的瓦楞纸板带织物输送带制作工艺
本专利技术涉及输送带的制作工艺，特别是一种瓦楞纸板生产运输中使用的专用输送带。
技术介绍
瓦楞纸板输送带无疑是瓦楞纸板生产线最重要的部件之一，它的品质高低对瓦楞纸板的质量具有决定性的影响，向来倍受纸箱厂和瓦线制造厂的关注。传统的针刺带结构为三层式：表面层、中间层和底面层，其表面层、底面层均为针刺植绒构造，中间层为经向粗纱加植绒构造，这种结构本身较为疏松，单位面积自重小，在受强拉力、加速运转时，不但施压和对纸板的携带能力极为有限，而且容易跑偏。它的延伸率较大，使用几个月就得重新剪接钢扣，费时费力，使生产受到影响。这也是针刺带多年来在市场上难以扩大份额的原因所在。透气性是瓦楞纸板输送带最重要的一个技术指标，与其相对应的瓦楞纸板的技术指标是水分含量。也就是说，瓦楞纸板所含水分的干燥是通过输送带来完成的，其工作流程是输送带将压力作用于纸板使其贴在加热板表面，吸收热量蒸发水蒸气，水蒸气被输送带吸收并在运行中散发掉。因此，对输送带的吸湿透气性能有着非常高的要求。现有技术中的瓦楞纸板生产线输送带，普遍具有以下问题：1、因为纱线的性能...
【技术保护点】
1.一种预先热处理的瓦楞纸板带织物输送带制作工艺，其特征在于，包括如下步骤：步骤1，预热处理：在纱线合股并捻前，将单股纱线在环境温度90℃‑160℃，蒸室压力2mpa‑4mpa，蒸室湿度大于90％的环境下，热处理45min‑60min；步骤2，合股并捻：将预热处理后的单股纱线合并成单捻的经线和纬线；步骤3，纺织织物输送带：将经线和纬线编织成织物输送带。
【技术特征摘要】
1.一种预先热处理的瓦楞纸板带织物输送带制作工艺，其特征在于，包括如下步骤：步骤1，预热处理：在纱线合股并捻前，将单股纱线在环境温度90℃-160℃，蒸室压力2mpa-4mpa，蒸室湿度大于90％的环境下，热处理45min-60min；步骤2，合股并捻：将预热处理后的单股纱线合并成单捻的经线和纬线；步骤3，纺织织物输送带：将经线和纬线编织成织物输送带。2.根据权利要求1所述的预先热处理的瓦楞纸板带织物输送带制作工艺，其特征在于：在步骤1中，纱线在环境温度140℃，蒸室压力3.5mpa，蒸室湿度大于100％的环境下，热处理60min。3.根据权利要求1所述的预先热处理的瓦楞纸板带织物输送带制作工艺，其特征在于：在步骤2中，将2根...
【专利技术属性】
技术研发人员：庄典飞，
申请(专利权)人：抚顺一元制带有限公司，
类型：发明
国别省市：辽宁,21