The invention discloses a preparation method of easily degradable environmental protection plastics, including: S01, ultrasonic sterilization of biological components; S02, mixing PVC monomer with plasticizer and other additives, adding biological components after dispersing, adding structural components after dispersing evenly, grinding and dispersing S03, obtained in S02; Adding coupling agent and crosslinking agent into the mixture, the mixture was grinded and dispersed by planetary grinder for 5 8 min at 300_400 r/min, and the required mixture was obtained; S04, the mixture of S03 was pelleted by twin screw extruder, the extrusion rate was 3.5_4.5 kg/h, the melting temperature was 205_210 C, and the desired degradable material was prepared. Masterbatch for environmentally friendly plastics. Compared with the plastic products of the prior art, the strength and toughness of the plastics in the present invention are basically the same. After being discarded, the plastics in the present invention can be broken slowly and degraded thoroughly in a humid and hot bacterial environment, and there is no pollution to the environment and human body, so it meets the requirements of environmental protection.
【技术实现步骤摘要】
一种易降解环保塑料的制备方法
本专利技术属于高分子材料领域,具体涉及一种易降解环保塑料的制备方法。
技术介绍
塑料工业在多年的发展过程中已形成门类非常齐全的工业体系,成为了与钢材、水泥、木材并驾齐驱的基础材料产业,作为轻工行业支柱产业之一,塑料行业以每年可观的增长速度保持着发展。我国是塑胶原料的生产大国,更是巨大的塑料制品的消费国,塑胶材料广泛应用于农林牧渔、日常生活和轻重工业领域中,成为一类不可或缺的生产资料。塑胶材料尽管拥有广泛的适用范围和低廉的应用成本等优点,但是其废弃物所造成的的污染与公害一直为人所诟病。近年来,针对塑料材料的相关环保产业的呼声也越来越高。塑料由于性能稳定,很难在短时间内被降解,许多大稳定性能的塑料需要百年甚至更长时间才能够完全被无害降解,目前针对塑料废弃物的处理方式主要为填埋,传统的焚烧等对环境造成强污染的处理方式已经被环保部门叫停。既想要获得塑料便利的使用性能和经济性,又想要塑料被废弃后能够迅速降解,许多研究者针对上述诉求进行了广泛的研究。可降解塑料即为解决上述塑料环保问题的良好替代品。目前可降解塑料主要分为生物可降解塑料和光降解塑料,由于光降解塑料需要加入光敏剂,一旦处于无光照条件下就停止发生降解反应(例如被填埋),在实际处理过程中,降解率并不高,故生物可降解塑料的适用性作为环保塑料来说更显著。现有技术中许多生物可降解塑料中都掺杂了较为大量的淀粉,利用淀粉的降解性提升塑料的降解性,但是淀粉含量过高对塑料的热塑性能、强度和拉伸性能影响比较大,难以达到常规塑料产品的使用要求。申请号为201110086963.4名为《一种易降解环保 ...
【技术保护点】
1.一种易降解环保塑料的制备方法,其特征在于包括如下步骤:S01,将生物性组分进行超声波灭菌处理,其中超声波频率范围为4100‑4200kHz,灭菌时间为5‑10分钟;S02,将聚氯乙烯单体与增塑剂和其他助剂混合,在200‑250r/min条件下分散10‑20分钟,然后加入S01中得到的生物性组分,分散均匀后加入结构性组分,在2000‑2500r/min条件下利用行星式研磨机进行研磨分散20‑30min;S03,在S02得到的混合物中加入偶联剂和交联剂,在300‑400r/min条件下利用行星式研磨机进行研磨分散5‑8min,得到所需混合原料;S04,将S03中混合原料利用双螺杆挤出机进行造粒,其挤出速率为3.5‑4.5kg/h,熔融温度为205‑210℃,制成所需易降解环保塑料的母粒。
【技术特征摘要】
1.一种易降解环保塑料的制备方法,其特征在于包括如下步骤:S01,将生物性组分进行超声波灭菌处理,其中超声波频率范围为4100-4200kHz,灭菌时间为5-10分钟;S02,将聚氯乙烯单体与增塑剂和其他助剂混合,在200-250r/min条件下分散10-20分钟,然后加入S01中得到的生物性组分,分散均匀后加入结构性组分,在2000-2500r/min条件下利用行星式研磨机进行研磨分散20-30min;S03,在S02得到的混合物中加入偶联剂和交联剂,在300-400r/min条件下利用行星式研磨机进行研磨分散5-8min,得到所需混合原料;S04,将S03中混合原料利用双螺杆挤出机进行造粒,其挤出速率为3.5-4.5kg/h,熔融温度为205-210℃,制成所需易降解环保塑料的母粒。2.如权利要求1所述易降解环保塑料的制备方法,其特征在于:所述环保塑料的组分及组分质量份数为:聚氯乙烯单体30-35份生物性组分25-28份结构性组分8-9份增塑剂3-4份偶联剂0.5-0.8份交联剂0.3-0.4份其他助剂2-3份。3.如权利要求1所述易降解环保塑料的制备方法,其特征在于:所述生物性组分及质量份数为:食用菌菌糠10-15份竹纤维粉2-4份糯米淀粉2-3份所述生物性组分的制备方法为:将食用菌菌糠粉碎至平均粒径为1-2mm,与平均长度为1-2mm、直径为3-5μm的竹纤维混合,混合均匀后在80-90℃烘箱内干燥至含水量低于20%,进行二次粉碎,粉碎至混合物平均粒...
【专利技术属性】