The invention belongs to the ceramic manufacturing field, in particular to a kiln glaze for firing light porcelain, a preparation method and a use method. The light porcelain low temperature kiln red spot glaze includes glass powder, transparent frit glaze, red pigment, nepheline powder, boric acid, kaolin, zinc oxide. This kind of kiln red spot glaze has the advantages of low cost, convenient use, low firing temperature and unique artistic feeling. The glaze produced by this kind of kiln has a red or copper-red background color, and irregular black spots are evenly distributed on the background color. The size and density of black spots vary according to the type of pottery and glazing thickness, which has a unique artistic effect. The porcelain made with this kind of glaze can improve the product grade and sale price, and has high economic value. In addition, this kind of glaze can be industrialized in batches, can be quickly popularized and used simply, and has strong competitiveness in the market.
【技术实现步骤摘要】
轻质瓷低温窑变红斑釉料的制备方法本申请是“轻质瓷低温窑变红斑釉料配方、制备及使用方法”的分案申请，原申请的申请日为2015年08月27日，申请号为：CN201510534705.6。
本专利技术属于陶瓷制造领域，具体涉及一种用于轻质瓷烧制的窑变釉料、制备方法及使用方法。
技术介绍
窑变釉即器物在窑内烧成时，由于窑中含有多种呈色元素，经氧化或还原作用，出窑后呈现意想不到的釉色效果。传统的窑变釉为中高温烧成，烧成温度在1200℃以上，烧成时间大都在12个小时以上，其烧成温度高、时间长，能源损耗大，导致成本高且不环保；而现有轻质白云陶窑变釉的釉面效果单一，品种单调，无法迎合不同个性的消费者需求。为解决上述问题，专利号为201110133469.9的专利技术专利公开了一种窑变釉白云陶及其制作工艺，该种窑变釉白云陶，包括白云陶坯体以及施于白云陶坯体表面上的釉层，该釉层包括直接施在白云陶坯体表面的底釉和施于底釉面上的面釉；底釉的各组分包括低温无铅熔块、着色氧化物、碳酸钙、碱土金属化合物、份高岭土；所述面釉的各组分按重量配比为低温无铅熔块、份氧化锌、份氧化钛、着色氧化物、份高岭...
【技术保护点】
1.轻质瓷低温窑变红斑釉料的制备方法，其特征在于，包括以下步骤：步骤一，按照釉料称重配比，将玻璃粉30‑45份、透明熔块釉25‑35份、霞石粉5‑10份、硼酸5‑10份、高岭土3‑8份、氧化锌2‑5份放入球磨罐中，并加入50‑60％的水；步骤二，球磨10‑15小时后，将红色料加入球磨罐中一起球磨20‑40分钟；步骤三，将步骤二获得的釉料过筛待用，制得窑变红斑釉料。
【技术特征摘要】
1.轻质瓷低温窑变红斑釉料的制备方法，其特征在于，包括以下步骤：步骤一，按照釉料称重配比，将玻璃粉30-45份、透明熔块釉25-35份、霞石粉5-10份、硼酸5-10份、高岭土3-8份、氧化锌2-5份放入球磨罐中，并加入50-60％...
【专利技术属性】
技术研发人员：李桂贤，刁龙海，
申请(专利权)人：福建省德化县冠鸿陶瓷有限公司，
类型：发明
国别省市：福建,35