The invention discloses an environment-friendly metal cutting fluid, which belongs to a metal cutting fluid suitable for metal processing in the field of mechanical processing technology. The environmental-friendly metal cutting fluid consists of 20-35 parts of barium sulfonate, 5-15 parts of borax, 20-30 parts of triethanolamine, 1-2 parts of methyl silicone oil, 1-5 parts of Calcium-magnesium ion softener, 5-15 parts of extreme pressure antiwear agent, and surplus water by weight. The EPA antiwear agent was synthesized by the reaction of oleic acid diethanolamide borate ester with hydroxymethylated benzotriazole, and then mixed with intermediate basic calcium sulfonate. The invention provides an environmental-friendly metal cutting fluid, which has the advantages of environmental protection, pollution-free, harmless effect on human body, excellent lubrication and wear resistance, avoiding the occurrence of cutting nodules and effectively protecting cutting tools.
【技术实现步骤摘要】
一种环保金属切削液
本专利技术属于机械加工
中适用于金属加工的一种金属切削液。
技术介绍
可持续发展问题是现今社会面临的重要问题之一，金属加工制造业也逐渐向绿色制造发展。金属切削加工是在大量使用切削液的基础上进行的，我国切削液的年使用量达到6万吨左右。随着制造业发展，金属切削液带来的环境问题日益凸显，因为开发合适的绿色切削液具有重要的意义。我国在水基切削液取得一定进展，但与国外水基切削液还存在一定差异，尤其表现在产品极压抗磨特性上。目前，关于硼酸酯的极压抗磨作用机理有两种看法；一种理论认为，硼酸酯分子在摩擦、磨损过程中发生聚合反应生成摩擦聚合物膜而改善了摩擦特性；另一种理论认为，硼酸酯能在摩擦金属表面形成几百纳米厚的非均相极压膜，膜的无机成分为B2O3和FeO，是无机膜的高强度起了极压润滑的作用。硼酸酯用做减摩、抗磨添加剂的研究结果表明，以0.5%~4.0%的添加量将硼酸酯添加到基础油中，能使摩擦系数下降5%~50%。磺酸钙不仅具有良好的极压抗磨性，而且它本身具有良好的防锈性能。它具有很高的碱保持能力，可以除去残留的酸性副产物，从而具有更好的防腐蚀性能，中和...
【技术保护点】
1.一种环保金属切削液，其特征在于，该环保金属切削液以重量份计由下列组分组成：石油磺酸钡20~35份、硼砂5~15份、三乙醇胺20~30份、甲基硅油1~2份、钙镁离子软化剂1~5份、极压抗磨剂5~15份，余量水；其中极压抗磨剂由油酸二乙醇酰胺硼酸酯与羟甲基化苯并三氮唑反应得到有机硼酸酯，然后与中碱性磺酸钙复配所得。
【技术特征摘要】
1.一种环保金属切削液，其特征在于，该环保金属切削液以重量份计由下列组分组成：石油磺酸钡20~35份、硼砂5~15份、三乙醇胺20~30份、甲基硅油1~2份、...
【专利技术属性】
技术研发人员：刘佳，
申请(专利权)人：武汉诺通润滑科技有限公司，
类型：发明
国别省市：湖北,42