一种含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢及其生产方法技术

本发明专利技术提供的一种含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢，含有以下重量百分比元素：碳0.13～0.18％、硅0.35～0.55％、锰1.30～1.50％、磷≤0.020％、硫≤0.010％、钒0.100～0.120％，Als 0.010～0.030％，余量为Fe和残余的微量杂质。与现有技术相比，采用本发明专利技术的技术方案生产的翼缘厚度40mm以下规格H型钢，屈服强度超过460MPa，其‑20℃低温韧性超过100J，具有较高的强度和良好低温韧性，提高了产品质量。

460MPa grade hot rolled H steel with vanadium bearing good low temperature toughness and its production method

The invention provides a 460 MPa grade hot-rolled H-beam containing vanadium with good low temperature toughness, which contains the following weight percentage elements: carbon 0.13-0.18%, silicon 0.35-0.55%, manganese 1.30-1.50%, phosphorus < 0.020%, sulfur < 0.010%, vanadium 0.100-0.120%, Als 0.010-0.030%, residual Fe and residual micro amount. Impurities. Compared with the prior art, the H-shaped steel with flange thickness of less than 40mm produced by the technical scheme of the invention has yield strength of over 460 MPa and low temperature toughness of more than 100J at

【技术实现步骤摘要】
一种含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢及其生产方法
本专利技术属于金属材料生产
,具体涉及一种含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢及其生产方法。
技术介绍
目前国家正大力推行钢结构建筑和绿色制造理念，国内钢铁产量快速增长，钢材的品种和规格逐步齐全，为我国建筑钢结构发展提供了良好的材料基础。为有效利用土地资源，建筑物不断地向高层化发展，而为更有效利用室内空间，对大跨度钢结构的需求不断增加，随着大量超高度、大跨度以及空间复杂钢结构的涌现，对钢材的性能和规格品种提出了更高要求尤其是对建筑用钢的强度要求越来越高。如已建的“鸟巢”、“央视”新台址和广州新电视塔等工程所用钢材已达Q390、Q420和Q460等级别。高强度的钢材可使建筑结构自重进一步减轻，并满足特殊、复杂结构的受力要求。
技术实现思路
本专利技术的目的在于提供一种含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢及其生产方法，生产的H型钢能够在屈服强度达到460MPa级别时仍具有良好的抗低温冲击韧性。本专利技术具体技术方案如下：一种含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢，本文档来自技高网...

【技术保护点】
1.一种含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢，其特征在于，所述含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢含有以下重量百分比元素：碳0.13～0.18％、硅0.35～0.55％、锰1.30～1.50％、磷≤0.020％、硫≤0.010％、钒0.100～0.120％，Als 0.010～0.030％，余量为Fe和残余的微量杂质。

【技术特征摘要】
1.一种含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢，其特征在于，所述含钒具有良好低温韧性的屈服强度460MPa级热轧H型钢含有以下重量百分比元素：碳0.13～0.18％、硅0.35～0.55％、锰1.30～1.50％、磷≤0.020％、硫≤0.010％、钒0.100～0.120％，Als0.010～0.030％，余量为Fe和残余的微量杂质。2.一种权利...

【专利技术属性】
技术研发人员：龚庆华，吴保桥，程鼎，石雷，张文满，彦井成，邢军，夏勐，汪杰，何军委，魏银丹，蒲玉梅，
申请(专利权)人：马钢集团控股有限公司，马鞍山钢铁股份有限公司，
类型：发明
国别省市：安徽,34