一种抗菌的聚酰胺隔热型材制造技术

一种抗菌的聚酰胺隔热型材，涉及型材加工制作技术领域，其特征在于：包括以下质量分的材料制成，聚酰胺66(PA66)35‑65份、聚酰胺6(PA6)5‑20份、聚酰胺6T(PA6T)5‑20份、聚酰胺9T(PA9T)5‑20份、玻璃纤维(GF)20‑60份、自制复合抗菌树脂包裹粉末10‑30份、润滑剂0.2‑1.5份、相容剂1.5‑5份、抗氧剂0.1‑0.6份、黑色母2‑8份。本发明专利技术方法合理、操作方便、抗菌、隔热。

An antibacterial polyamide heat insulation profile

The utility model relates to an antibacterial polyamide heat insulation profile, which relates to the technical field of profile processing and manufacturing, and is characterized in that the profile comprises a material made of the following quality components: polyamide 66 (PA66) 35_65 parts, polyamide 6 (PA6) 5_20 parts, polyamide 6T (PA6T) 5_20 parts, polyamide 9T (PA9T) 5_20 parts, glass fiber (GF) 20_60 parts, self-made composite antibacterial material. Resin-coated powders 10 30 phr, lubricants 0.2 1.5 phr, compatibilizers 1.5 5 phr, antioxidants 0.1 0.6 phr, black mother 2 8 phr. The invention has the advantages of reasonable method, convenient operation, antibacterial and heat insulation.

【技术实现步骤摘要】
一种抗菌的聚酰胺隔热型材
本专利技术涉及型材加工制作
，具体涉及一种抗菌的聚酰胺隔热型材。
技术介绍
聚酰胺隔热型材是目前一种断桥铝合金隔热节能门窗中连接内、外铝合金型材的非金属连接件，在起到连续内外结构力学作用的同时也是起到隔断铝合金门窗框上热传递的作用，其原料主要是由聚酰胺66树脂、其它树脂和玻璃纤维改性而成。使用这种隔热型材的铝合金门窗具有传热系数小、隔热隔音防尘的效果。聚酰胺隔热型材在与铝型材复合后，型材表面会存在凹面和连接缝隙(简称为断桥区域)，门窗在使用过程中，大自然中的雨水、粉尘等等会积聚在门窗这些部位，这给细菌的形成提供一个培养空间。另外，由于断桥隔热门窗的隔热作用，使用之后会使门窗内外形成较大的温度差，特别是在低温天气时，空气中的湿气会在门窗上冷凝结露，在型材断桥区域积累大量湿气，细菌、病菌将会大量滋生，危及消费者使用安全。由于细菌、病菌等很难在金属上滋生，并且滋生后的清洁、杀菌消毒都会很方便，而聚酰胺隔热型材属于嵌入复合在铝合金门窗上，消毒过程不方便也不彻底。目前门窗设计人员在隔热条的形状和门窗结构上进行改变来避免凹面和连接缝隙的存在，但这不能从根源上解决型本文档来自技高网...

【技术保护点】
1.一种抗菌的聚酰胺隔热型材，其特征在于：包括以下质量分的材料制成，

【技术特征摘要】
1.一种抗菌的聚酰胺隔热型材，其特征在于：包括以下质量分的材料制成，2.根据权利要求1所述的一种抗菌的聚酰胺隔热型材，其特征在于：所述一种抗菌的聚酰胺隔热型材的制备方式为：将自制复...

【专利技术属性】
技术研发人员：李守宏，
申请(专利权)人：金寨宏伟新材料有限公司，
类型：发明
国别省市：安徽,34