The invention discloses a fire-proof, insulation and sound-proof cement polystyrene mold shell, which comprises the following raw materials: polystyrene particles, cement, latex powder, water reducing agent and water. The fire-proof and sound-proof cement polystyrene mold shell of the invention has the advantages of good flame retardancy, non-burning, non-toxic smell emission, wall heat preservation and insulation, making people feel warm in winter and cool in summer, and polystyrene mold shell also has good sound insulation effect. Compared with the existing thermal insulation building, it can increase the indoor use area, save formwork, convenient construction, save labor and time significantly, and reduce economic costs.
【技术实现步骤摘要】
一种防火保温隔音水泥聚苯模壳
本专利技术涉及一种防火保温隔音水泥聚苯模壳。
技术介绍
节约能源同时又让人们感受到住宅的安全与舒适，这是社会发展的必然趋势。国家不仅要求新建筑采用节能设计施工、对旧建筑也要采取节能补救措施。建筑节能已迫在眉睫。人们希望自己的居室安全，能抗震并希望能抵抗历史最高震级；希望建材阻燃，以利火灾控制；希望居室保温，有“冬暖夏凉”之感；希望居室隔音，日常声响不致侵扰四邻。过去的砖砼结构显然不符合今天的需求，不但不符合抗震要求，更不符合保温节能要求。过去的外墙围护结构通常为粘土砖，其厚度在东北地区为365、490、620mm，这种墙材的导热系数过大，墙体平均传热系数1.6W/(m·K)左右。在严寒季节，外墙内表面的温度低于室内空气露点温度时，外墙的内表面就产生结露引发内墙面长霉现象。这种现象不但会影响人们舒适和健康，同时也造成室内用具及房屋结构损坏；还有隔音效果差以及它的抗震问题更令人担忧。用于建筑外墙的保温材料主要包括三大类：①以矿物棉和玻璃棉为主的无机保温材料，通常认定为不燃性材料，岩棉、矿渣棉在常温条件下它们的导热系数通常在0.036～0....
【技术保护点】
1.一种防火保温隔音水泥聚苯模壳，其特征在于，包括下述原料制备而成：聚苯颗粒、水泥、乳胶粉、减水剂、水。
【技术特征摘要】
1.一种防火保温隔音水泥聚苯模壳，其特征在于，包括下述原料制备而成：聚苯颗粒、水泥、乳胶粉、减水剂、水。2.一种防火保温隔音水泥聚苯模壳，其特征在于，包括下述重量份的原料制备而成：5-10份聚苯颗粒、240-280份水泥、0.3-3份乳胶粉、1-5份减水剂、70-130份水。3.一种防火保温隔音水泥聚苯模壳，其特征在于，包括下述重量份的原料制备而成：5-10份聚苯颗粒、240-280份水泥、0.3-3份乳胶粉、1-5份减水剂、0.2-2份界面剂、70-130份水。4.根据权利要求3所述的防火保温隔音水泥聚苯模壳，其特征在于，所述界面剂的制备方法如下：将300-900g脱脂大豆粉加入1000-3000g水中，加入30-60g邻苯二甲酸二乙酯，升温至45-52℃，在45-52℃、以100-500转/分钟转速搅拌1-5小时，得到混合料A，将10-40g固化剂、10-40gDMP-30、15-45g改性剂、16-32g衣康酸、40-90g乙烯基三乙氧基硅烷、15-45g二缩水甘油醚、3-15g偶联剂、50-300g水混合，升温至45-52℃，在45-52℃、转速为100-500转/分钟搅拌20-80分钟，得到混合料B，将混合料B加入到混合料A中，在45-52℃、以100-500转/分钟搅拌1...
【专利技术属性】
技术研发人员：张如心，董旭，于海洋，李鑫恒，
申请(专利权)人：北京窝牛新能源科技有限公司，
类型：发明
国别省市：北京,11