The invention discloses a waterproof and antibacterial coating for building interior wall used in mildew environment and a manufacturing process thereof. The waterproof and antibacterial coating for building interior wall used in mildew environment is prepared from the following weight components: polyurethane formate resin 80_100 parts, polyvinylpyrrolidone 4_10 parts, diethylene glycol 4_10 parts, nano silver 1_5 parts. The invention reduces the thickening agent such as cellulose by inorganic thickening agent, which may decompose into monosaccharide and easily lead to mildew of paint. The possibility of change, and the polyurethane formate resin and diethylene glycol dispersant can effectively ensure the dispersion of nano-silver in the paint, prevent nano-silver adsorption and agglomeration.
【技术实现步骤摘要】
一种应用于霉菌环境的建筑内墙防水抗菌涂料及其制备方法
本专利技术涉及一种建筑涂料领域，具体是一种应用于霉菌环境的建筑内墙防水抗菌涂料及其制备方法。
技术介绍
随着涂料的用途的不断细化，市场上出现了许多针对霉菌环境的防水抗菌涂料，随着纳米技术的不断发展，在一般的水性涂料中添加纳米颗粒可以极大的改善涂料的一些功能特性，对于抗菌方面，市场上的抗菌涂料多采用对涂料内添加纳米银或者其他纳米氧化金属来实现涂料的抗菌性，但是涂料的抗菌性能参差不一，主要原因是首先纳米材料在涂料中的稳定分散问题，由于纳米粒子比表面积和表面张力都很大，容易吸附而发生团聚，在溶液中将其有效地分散成纳米级粒子是非常困难的，寻找合适的分散剂来分散纳米材料，并采用合适的稳定剂将良好分散的纳米材料粒径稳定在纳米级，是纳米技术在涂料改性中获得广泛应用必须解决的最关键问题。而且市场上的一些抗菌涂料，在添加增稠剂时，多使用纤维素类增稠剂，纤维素类增稠剂属天然高分子化合物，易受到霉菌攻击，降解为单糖，使黏度下降，因此在对生产过程的卫生条件要求严格，因此，针对这些问题，我们需要一种可以有效保证纳米银等抗菌纳米材料的分散...
【技术保护点】
1.一种应用于霉菌环境的建筑内墙防水抗菌涂料，其特征在于，由下述重量份的原料制成：聚氨酯甲酸酯树脂80‑100份、聚乙烯吡咯烷酮4‑10份、二甘醇4‑10份、纳米银1‑5份、纳米二氧化钛1‑5份、新戊二醇二缩水甘油醚3‑10份、膨润土1‑5份、硅酸铝1‑2份、丙烯酸类树脂2‑8份、颜料1‑10份、酮亚胺1‑2份。
【技术特征摘要】
1.一种应用于霉菌环境的建筑内墙防水抗菌涂料，其特征在于，由下述重量份的原料制成：聚氨酯甲酸酯树脂80-100份、聚乙烯吡咯烷酮4-10份、二甘醇4-10份、纳米银1-5份、纳米二氧化钛1-5份、新戊二醇二缩水甘油醚3-10份、膨润土1-5份、硅酸铝1-2份、丙烯酸类树脂2-8份、颜料1-10份、酮亚胺1-2份。2.根据权利要求1所述的应用于霉菌环境的建筑内墙防水抗菌涂料，其特征在于，由下述重量份的原料制成：聚氨酯甲酸酯树脂90-100份、聚乙烯吡咯烷酮8-10份、二甘醇6-10份、纳米银1-3份、纳米二氧化钛1-3份、新戊二醇二缩水甘油醚6-10份、膨润土1-3份、硅酸铝1-2份、丙烯酸类树脂2-4份、颜料1-5份、酮亚胺1-2份。3.根据权利要求1所述的应用于霉菌环境的建筑内墙防水抗菌涂料，其特征在于，由下述重量份的原料制成：聚氨酯甲酸酯树脂100份、聚乙烯吡咯烷酮10份、二甘醇10份、纳米...