The invention relates to a Co/Ni_MoO2 composite electrolytic water hydrogen production catalyst and a preparation method thereof, belonging to the technical field of preparing inorganic nano-materials. The Co/Ni_MoO2 catalyst is prepared by grinding and mixing four kinds of precursors, cobalt nitrate, nickel nitrate, ammonium molybdate and F127, and then heating. The specific steps are as follows: firstly, the dough precursor was prepared by mixed grinding with cobalt nitrate, nickel nitrate, ammonium molybdate and F127 as reactants, and then the Co/Ni_MoO2 composite catalyst was prepared by heating at 70 and 300 degrees Celsius respectively.
【技术实现步骤摘要】
一种Co/Ni-MoO2复合电解水催化剂的制备方法
本专利技术涉及一种Co/Ni-MoO2复合电解水制氢催化剂及其制备方法，属于无机纳米材料
技术介绍
随着传统化石燃料的不断消耗以及环境污染的日益加剧，再生清洁能源受到了越来越广泛的关注。氢能具有能量密度高、清洁环保等特点，被认为是优异的化石燃料替代品。通过电解水的方法可以方便的制备氢气，满足实际应用需求。但是，由于水裂解反应为非自发反应，其吉布斯自由能变高达237kJ/mol，使得电解水过程中的电能消耗较大。铂族金属常被用作电解水的催化剂以降低水裂解过程中的电能消耗，但是其价格过于昂贵，无法广泛使用。因而，开发价格便宜的电解水催化剂，对于减少电解水过程中的能源消耗，减少铂等贵金属的用量，降低电解水的成本具有重要的意义。MoO2具有接近金属的良好导电性，且化学稳定性高、价格便宜，有望成为一类重要的电解水催化剂。但是在电解水过程中，MoO2会和氢自由基之间形成键能很强的金属氢化物，从而降低了反应速率。将过渡金属修饰到MoO2基体中，制备过渡金属-MoO2复合催化剂是解决这一问题的常见方法。例如，L.J.Ya...
【技术保护点】
1.一种Co/Ni‑MoO2复合电解水制氢催化剂的制备方法，其特征在于制备方法的步骤如下：1）通过混合研磨的方法以硝酸钴、硝酸镍、钼酸铵和F127为反应物制得面团状的前驱体混合物；2）将步骤1所得面团状混合物置于马弗炉中，先在70摄氏度下加热5小时，然后将温度升高至300摄氏度加热1小时后自然降温至室温即得到Co/Ni‑MoO2复合电解水制氢催化剂。
【技术特征摘要】
1.一种Co/Ni-MoO2复合电解水制氢催化剂的制备方法，其特征在于制备方法的步骤如下：1）通过混合研磨的方法以硝酸钴、硝酸镍、钼酸铵和F127为反应物制得面团状的前驱体混合物；2）将步骤1所得面团状混合物置于马弗炉中，先在70摄氏度下加热5小时，然后将温度升高至300摄氏度加热1小时后自然降温至室温即得到Co/Ni-MoO2复合电...
【专利技术属性】
技术研发人员：陈志明，杨晓东，王晓梅，徐波，李村成，
申请(专利权)人：济南大学，
类型：发明
国别省市：山东,37