The invention relates to a wet-curing polyurethane hot-melt adhesive for automobile lamps and a preparation method thereof. The raw materials include polyester polyol, 10-45 phr; polyether polyol, 20-55 phr; polyacrylic resin, 10-45 phr; chain extender, 0.01_5 phr; isocyanate, 10-20 phr; catalyst, 0.0001-0.001 phr. The wet curing polyurethane hot melt adhesive for automotive lamps is prepared by copolymerization of polyols containing active groups (hydroxyl groups) with isocyanate groups (NCO). The end of the polymer chain contains the active group NCO, and NCO reacts irreversibly with air or water in the adhesives, resulting in high adhesion. Strength.
【技术实现步骤摘要】
一种用于车灯的湿固化聚氨酯热熔胶及制备方法
本专利技术涉及一种用于车灯的湿固化聚氨酯热熔胶及制备方法，属于一种反应型聚氨酯热熔胶，属于聚氨酯热熔胶制备
技术介绍
中国专利技术专利申请公开说明书CN102585753A公开了一种用于汽车灯具密封用的聚氨酯热熔胶。其将高结晶性聚酯二醇、聚酯多元醇、增粘树脂在搅拌下真空脱水，然后降温；取二异氰酸酯预热，加入反应釜搅拌均匀，进行预聚反应；预聚完成后在氮气环流下依次加入计量好的催化剂、抗氧剂、偶联剂、粘度稳定剂、灰色浆搅拌至混合均匀；在通入氮气保护条件下出料，密封包装，即得产物车灯粘接用聚氨酯热熔胶。但是其优点在于粘接强度高、耐震动性好、对环境友好，但该热熔胶的多元醇全部用聚酯多元醇为原料，制备的聚氨酯热熔胶粘度较高，对于使对温度相对敏感的基材易受损伤，如ABS，PVC和TPU膜材等。中国专利技术专利申请公开说明书CN103740316A公开了一种用于汽车灯具密封用的聚氨酯热熔胶。将聚酯多元醇与异氰酸酯在一定温度搅拌下进行预聚反应，预聚完成后加入催化剂和炭黑，抽真空脱除气泡30min，在通入氮气保护条件下倒出产物，...
【技术保护点】
1.一种用于车灯的湿固化聚氨酯热熔胶，其特征在于：按质量份数计，其原料包括聚酯多元醇，10－45份；聚醚多元醇，20－55份；聚丙烯酸树脂，10－45份；扩链剂，0.01‑5份；异氰酸酯，10－20份；催化剂，0.0001－0.001份。
【技术特征摘要】
1.一种用于车灯的湿固化聚氨酯热熔胶，其特征在于：按质量份数计，其原料包括聚酯多元醇，10－45份；聚醚多元醇，20－55份；聚丙烯酸树脂，10－45份；扩链剂，0.01-5份；异氰酸酯，10－20份；催化剂，0.0001－0.001份。2.根据权利要求1所述的用于车灯的湿固化聚氨酯热熔胶，其特征在于：所述聚丙烯酸树脂的分子量Mn为1000-1000000，玻璃化转变温度Tg为30-120℃。3.根据权利要求2所述的用于车灯的湿固化聚氨酯热熔胶，其特征在于：所述聚丙烯酸树脂的分子量Mn为5000-90000，玻璃化转变温度Tg为40-90℃。4.根据权利要求1所述的用于车灯的湿固化聚氨酯热熔胶，其特征在于：所述扩链剂为1，4-丁二醇、乙二醇、丙二醇、一缩二乙二醇、新戊二醇、丙三醇、三羟甲基丙烷、3,3'-二氯-4,4'-二氨基二苯基甲烷、乙醇胺、二乙醇胺、三乙醇胺、...
【专利技术属性】
技术研发人员：吴键儒，平川，
申请(专利权)人：嘉兴市建川新材料科技有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。