The invention relates to a polyurethane hot melt adhesive, the components and the weight percentage are: Papi: 40 ~ 65%, the crystallinity of polymer polyol: 10 ~ 20%, ethylene vinyl acetate copolymer: 10 ~ 20%, 5 ~ 10%: modified resin, acid stabilizer: 0.001 ~ 0.01% from 1 to 5%, antioxidant, crosslinking agent: 1 ~ 5%, 2 ~ 3% curing agent, curing catalyst two ether: 0.02 ~ 0.1%. The invention has the advantages that the modified polyurethane resin in the raw material of the polyurethane hot-melt adhesive can effectively improve the impact resistance and the adhesive strength of the adhesive, and the preparation efficiency is high.
【技术实现步骤摘要】
一种聚氨酯热熔胶黏剂
本专利技术涉及换一种胶黏剂,特别涉及一种聚氨酯热熔胶黏剂。
技术介绍
热熔胶黏剂是一种在熔融条件下进行涂布,经硬化或结晶产生强度的胶黏剂,热熔胶黏剂的涂布不需要溶剂,热熔胶黏剂的市场需求量在不断增加。传统的热熔胶黏剂制备效率较低,同时粘结效果较差,因此急需研制一种制备效率高、粘结效果好的聚氨酯热熔胶黏剂,经检索,未发现与本专利技术相同或相似的技术方案。
技术实现思路
本专利技术要解决的技术问题是提供一种制备效率高、粘结效果好的聚氨酯热熔胶黏剂。为解决上述技术问题,本专利技术的技术方案为:一种聚氨酯热熔胶黏剂,其创新点在于:所述成分及其重量百分比分别为:多亚甲基多苯基多异氰酸酯:40~65%,结晶性聚合物多元醇:10~20%,乙烯-醋酸乙烯共聚物:10~20%,改性树脂:5~10%,酸性稳定剂:0.001~0.01%,抗氧化剂:1~5%,交联剂:1~5%,固化剂2~3%,固化反应催化剂二醚:0.02~0.1%。进一步的,所述固化剂选用羟基苯磺酸,交联剂选用过氧化二异丙苯,抗氧化剂选用没食子酸丙酯。进一步的,所述多亚甲基多苯基多异氰酸酯占50%,结晶性聚合物多元醇占15%,乙烯-醋酸乙烯共聚物占10%,改性树脂占5%,酸性稳定剂占0.005%,抗氧化剂占2%,交联剂占2%,固化剂占2%,固化反应催化剂二醚占0.05%。进一步的,所述多亚甲基多苯基多异氰酸酯占65%,结晶性聚合物多元醇占25%,乙烯-醋酸乙烯共聚物占20%,改性树脂占10%,酸性稳定剂占0.01%,抗氧化剂占2%,交联剂占2%,固化剂占2%,固化反应催化剂二醚占0.08%。本专 ...
【技术保护点】
一种聚氨酯热熔胶黏剂,其特征在于:所述成分及其重量百分比分别为:多亚甲基多苯基多异氰酸酯:40~65%,结晶性聚合物多元醇:10~20%,乙烯‑醋酸乙烯共聚物:10~20%,改性树脂:5~10%,酸性稳定剂:0.001~0.01%,抗氧化剂:1~5%,交联剂:1~5%,固化剂2~3%,固化反应催化剂二醚:0.02~0.1%。
【技术特征摘要】
1.一种聚氨酯热熔胶黏剂,其特征在于:所述成分及其重量百分比分别为:多亚甲基多苯基多异氰酸酯:40~65%,结晶性聚合物多元醇:10~20%,乙烯-醋酸乙烯共聚物:10~20%,改性树脂:5~10%,酸性稳定剂:0.001~0.01%,抗氧化剂:1~5%,交联剂:1~5%,固化剂2~3%,固化反应催化剂二醚:0.02~0.1%。2.根据权利要求1所述的一种聚氨酯热熔胶黏剂,其特征在于:所述固化剂选用羟基苯磺酸,交联剂选用过氧化二异丙苯,抗氧化剂选用没食子酸丙酯。3.根据权利要求1所述的一种聚氨酯热熔...
【专利技术属性】
技术研发人员:张孝俤,李小静,
申请(专利权)人:江苏国胶化学科技有限公司,
类型:发明
国别省市:江苏,32