The invention belongs to the technical field of building decorative materials, and discloses a film used for formaldehyde-free environmental protection wood flooring and a preparation method thereof. According to the mass fraction, the film comprises the following components: 100 parts HDPE, 1-15 parts EVA, 1-20 parts MA_PE (maleic anhydride grafted polyethylene) and 0-20 parts filler. After mixing the mixture according to the mass fraction of each component, the formula mixture is plasticized by extruder, the plasticizing temperature is 180-210 C, blown into foam, air-cooled at 20-25 C, drawn, trimmed and rolled into film. The process of the invention is simple, and the film used for the formaldehyde-free environmental protection wood floor provided by the invention can be used to produce waterproof, insect-proof, glue-free, formaldehyde-free, odor-free and environmental protection wood floor.
【技术实现步骤摘要】
一种用于无甲醛环保木地板的薄膜及其制备方法
本专利技术属于建筑装饰材料制作
，尤其涉及一种用于无甲醛环保木地板的薄膜及其制备方法。
技术介绍
目前，业内常用的现有技术是这样的：传统的实木地板或实木复合地板的耐候性较差，在湿度和温度变化较大的环境中长期使用时，容易产生变形和开裂。现有复合木地板一般采用含甲醛密度板与耐磨层、平衡层、芯纤层压粘而成。作为密度板粘合剂的甲醛胶中的甲醛，在常温下会向空气中缓慢持续地挥发，导致室内甲醛含量大幅度提高，可以使人在不知不觉中中毒，出现眼鼻喉刺激感、眼睛流泪、疲劳乏力、记忆减退、头痛、发烧、哮喘、过敏性肺炎、皮肤炎等症状，此即所谓的“大厦症候群”以及“化学物质过敏症”。综上所述，现有技术存在的问题是：(1)现有木地板防水、防潮效果差；(2)用胶水复合的地板含有甲醛，缓慢释放，不卫生环保。本专利技术可以解决以上问题，使用刨切木片来生产陈本大大低于实木地板。解决上述技术问题的难度和意义：解决以上技术问题的关键是薄膜，要求薄膜有一定的刚性和强度，有别于胶水，还要求薄膜与木片有很好的粘合力，薄膜与木片层叠加压加热可以熔化成为整体。所以...
【技术保护点】
1.一种用于无甲醛环保木地板的薄膜，其特征在于，所述用于无甲醛环保木地板的薄膜按质量分数计由HDPE 100份、EVA 1～15份、马来酸酐接枝聚乙烯1～20份和填料0～20份组成。
【技术特征摘要】
1.一种用于无甲醛环保木地板的薄膜，其特征在于，所述用于无甲醛环保木地板的薄膜按质量分数计由HDPE100份、EVA1～15份、马来酸酐接枝聚乙烯1～20份和填料0～20份组成。2.一种如权利要求1所述的用于无甲醛环保木地板的薄膜的制备方法，其特征在于，包括以下步骤：(1)按照各组分的质量分数进行混合配比；(2)使用挤出机使配方混合料塑化，塑化温度180～210℃；(3)吹塑成泡，20...
【专利技术属性】
技术研发人员：林渊智，苏羽航，刘毅，段宁宁，
申请(专利权)人：福建师范大学福清分校，
类型：发明
国别省市：福建,35
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。