The invention discloses a production method of zinc stearate, which relates to the technical field of chemical synthesis. The zinc stearate is prepared by reacting each component of the following weight parts: 800 1200 parts of stearate, 140 170 parts of zinc oxide, 5 15 parts of catalyst, 50 70 parts of deionized water; The catalyst comprises acetic acid, hydrogen peroxide and hydrogen oxidation. Potassium solution and ammonia. The invention obtains zinc stearate product with excellent comprehensive performance by a new low temperature and high pressure powder method, omits the pressing process and the drainage process, effectively shortens the reaction time, reduces the production energy consumption, improves the production efficiency, stabilizes the product quality and has good dispersion effect.
【技术实现步骤摘要】
一种硬脂酸锌的生产方法
本专利技术涉及化工合成
，特别涉及一种硬脂酸锌的生产方法。
技术介绍
硬脂酸锌是一种广泛应用于聚烯烃、聚氯乙烯树脂生产的润滑剂、脱模剂，市场需求量大。目前常用的硬脂酸锌生产工艺主要有复分解法、水介质催化法及熔融法等，主要存在设备昂贵、操作繁琐、生产能耗高及污染严重等问题，影响生产效率，高效、节能、环保的硬脂酸锌生产方法，是提高生产效率，降低生产成本的关键。另外，由于硬脂酸锌不溶于水，产品是以粒子形式分散于体系中，因此，硬脂酸锌粒径的大小直接影响其有效成分的分散效果，目前的产品大多存在粒径较大、不易分散及容易沉淀等问题，使用效果较差，控制产品粒径是提高硬脂酸锌使用效果的关键。
技术实现思路
本专利技术旨在提供一种硬脂酸锌的生产方法，通过新型低温高压粉末法得到综合性能优异的硬脂酸锌产品，省略压片与排水工序，缩短反应时间，减少生产能耗，提高生产效率，提升产品品质。为了实现本专利技术的技术目的，本专利技术一种硬脂酸锌的生产方法的技术方案是：一种硬脂酸锌的生产方法，所述硬脂酸锌由下列重量份数的各组分反应制得：硬脂酸800-1200份，氧化锌140-...
【技术保护点】
1.一种硬脂酸锌的生产方法，其特征在于：所述硬脂酸锌由下列重量份数的各组分反应制得：硬脂酸800‑1200份，氧化锌140‑170份，催化剂5‑15份，去离子水50‑70份；所述硬脂酸锌的生产方法，包括以下步骤：（1）将800‑1200份的所述硬脂酸与140‑170份的所述氧化锌投入反应釜中，升温至57‑65℃后，开始搅拌，搅拌8‑15min后，加入5‑15份的所述催化剂和50‑70份的所述去离子水，盖好所述反应釜的釜盖，继续升温进行反应；（2）所述反应釜内温度升至75‑80℃时开始反应，继续升温至93‑98℃时停止加热，保持温度稳定，反应18‑25min至所述反应釜内压力...
【技术特征摘要】
1.一种硬脂酸锌的生产方法，其特征在于：所述硬脂酸锌由下列重量份数的各组分反应制得：硬脂酸800-1200份，氧化锌140-170份，催化剂5-15份，去离子水50-70份；所述硬脂酸锌的生产方法，包括以下步骤：（1）将800-1200份的所述硬脂酸与140-170份的所述氧化锌投入反应釜中，升温至57-65℃后，开始搅拌，搅拌8-15min后，加入5-15份的所述催化剂和50-70份的所述去离子水，盖好所述反应釜的釜盖，继续升温进行反应；（...
【专利技术属性】
技术研发人员：谭学政，潘学良，孟庆举，蒋建林，
申请(专利权)人：山东三义实业股份有限公司，
类型：发明
国别省市：山东,37