The invention provides a high performance HXNBR oligomer ester masterbatch and a preparation method thereof. HXNBR oligopolyester masterbatch was prepared by blending oligopolyester with HXNBR by pre-dispersing technology, adding a quantitative mixing accelerator and filler, mixing, extruding and granulating. Compared with the direct addition of oligopolyester, the masterbatch rubber can effectively avoid the problems of sticking rolls and long mixing time in the later processing, improve the utilization of oligopolyester, and further improve the properties of HXNBR rubber products. The invention can be widely used in various rubber oil compounding agent masterbatch refining, especially suitable for high performance and multi-function oligoester masterbatch refining.
【技术实现步骤摘要】
一种高性能HXNBR齐聚酯母炼胶及其制备方法
本专利技术属于橡胶类复合材料制备
，特别是具有高性能HXNBR齐聚酯母炼胶及其应用领域。
技术介绍
橡胶是工业生产中的重要基础材料。在橡胶制品的原材料中，齐聚酯是一类多功能油类配合剂。一方面，在橡胶加工过程中，油类的齐聚酯能够起到软化油的作用，有利于橡胶的加工成型，另一方面，齐聚酯中含有不饱和双键，能在后期橡胶的硫化过程中，参与硫化反应，从而实现了对橡胶制品的增强作用。但是，齐聚酯在加入过程中存在诸多问题，例如，粘稠状齐聚酯的称量和加料都比较困难，会在容器内粘壁，计量容易出现误差；炼胶初期，齐聚酯的加入导致橡胶在炼胶设备上打滑，不利于炼胶；炼胶后期，齐聚酯会导致胶料严重粘辊，导致混炼时间延长，降低生产效率。因此，如何将油类齐聚酯较好的加入到橡胶中，避免加工问题，同时能发挥齐聚酯的最大功能，是目前橡胶工业中的热点问题之一。
技术实现思路
本专利技术的目的在于提供一种高性能HXNBR齐聚酯母炼胶及制备方法。一种高性能HXNBR齐聚酯母炼胶，其特征在于包括以下组分：HXNBR100质量份，齐聚酯100-200质量份，促进剂...
【技术保护点】
1.一种高性能HXNBR齐聚酯母炼胶，其特征在于包括以下组分：HXNBR 100质量份，齐聚酯100‑200质量份，促进剂2‑4质量份，防老剂2‑4质量份，填充剂5‑15质量份，甲基丙烯酸锌8‑15质量份，过氧化二异丙苯0.5‑1质量份，硬脂酸铬2‑5质量份。
【技术特征摘要】
1.一种高性能HXNBR齐聚酯母炼胶，其特征在于包括以下组分：HXNBR100质量份，齐聚酯100-200质量份，促进剂2-4质量份，防老剂2-4质量份，填充剂5-15质量份，甲基丙烯酸锌8-15质量份，过氧化二异丙苯0.5-1质量份，硬脂酸铬2-5质量份。2.根据权利要求1所述的一种高性能HXNBR齐聚酯母炼胶，其特征在于，所述的促进剂为TMTD和NS的2:1混合物。3.根据权利要求1所述的一种高性能HXNBR齐聚酯母炼胶，其特征在于，所述的填充剂为N330和N774的一种或两...