The invention discloses a water bath annealing liquid for continuous drawing. It consists of 14.18 parts triethanolamine, 10.14 parts acrylic acid, 8.12 parts phosphate, 4.8 parts sodium silicate and 50.60 parts distilled water. The copper wire is annealed and annealed after drawing, cooling and lubrication by continuous annealing water. The present invention uses continuous plating water annealing liquid to replace traditional oil anneal liquid, the concentration of degreasing agent required by electroplating pretreatment is reduced by half, the consumption of degreasing agent is reduced, the current consumption liquid of oil removal is reduced by 30%, the cost of oil removing agent is reduced by 45%, and the cost is saved.
【技术实现步骤摘要】
连拉连镀水性退火液
:本专利技术属于铜线镀锡
,特别涉及一种连拉连镀水性退火液。
技术介绍
:传统连拉连镀中,退火工艺与普通大拉一样,为了达到清洗、冷却、收线润滑等作用,退火液往往使用0.5%-1.0%的拉丝油作为退火液,由于电镀时为了得到更好的镀层结合率,电镀之前必需要脱脂。传统工艺由于带出和蒸发的双重消耗,因此拉丝油消耗量比较大,而且随着国家环保刚性要求越来越高,无论企业自身对于成本压缩的自身诉求,还是国家环保的外部要求都需要对现有退火液工艺进行改进。公开于该
技术介绍
部分的信息仅仅旨在增加对本专利技术的总体背景的理解,而不应当被视为承认或以任何形式暗示该信息构成已为本领域一般技术人员所公知的现有技术。
技术实现思路
:本专利技术的目的在于提供一种连拉连镀水性退火液,从而克服上述现有技术中的缺陷。为实现上述目的,本专利技术提供了一种连拉连镀水性退火液,其组分为14-18份的三乙醇胺、10-14份的丙烯酸、8-12份的磷酸酯、4-8份的硅酸钠、50-60份的蒸馏水。一种连拉连镀工艺,其特征在于:采用连拉连镀水性退火液对拉丝退火后的铜线进行清洗、冷却、润滑。与现有技术相比,本专利技术具有如下有益效果:采用连拉连镀水性退火液代替传统油性退火液,电镀预处理脱脂所需的除油剂浓度降低了一半,降低了除油剂消耗,除油所需的电流消耗液降低了30%,除油剂处理费用降低45%,节省成本。具体实施方式:下面对本专利技术的具体实施方式进行详细描述,但应当理解本专利技术的保护范围并不受具体实施方式的限制。除非另有其它明确表示,否则在整个说明书和权利要求书中,术语“包括”或其变换如 ...
【技术保护点】
1.一种连拉连镀水性退火液,其特征在于:其组分为14‑18份的三乙醇胺、10‑14份的丙烯酸、8‑12份的磷酸酯、4‑8份的硅酸钠、50‑60份的蒸馏水。
【技术特征摘要】
1.一种连拉连镀水性退火液,其特征在于:其组分为14-18份的三乙醇胺、10-14份的丙烯酸、8-12份的磷酸酯、4-8份的硅酸钠、5...