The invention discloses a concrete anti cracking agent, which is characterized by the weight ratio of each component as follows: 8 of 10 parts of industrial anhydrous aluminum sulfate, 10 to 15 parts of anhydrite, 2 to 5 high strength imitation steel fiber, 0.1 to 0.5 portion of twelve alkyl sulphate, 5 of 10 copies of silica fume, 0.5 2 carboxymethyl cellulose, 0.5 Aluminate clinker, 5, 10, Magnesium Oxide, 2, 5 active activator. The invention provides a concrete anti crack agent, which can enhance the anti cracking ability of concrete members under the action of transverse and vertical seismic waves produced by the earthquake, and reduce the impact of seismic waves on the beating and swinging of concrete structures, and thus ensure the durability of the building.
【技术实现步骤摘要】
一种混凝土抗裂剂
本专利技术涉及建筑材料领域，尤其涉及一种混凝土抗裂剂。
技术介绍
目前国内尚无混凝土抗震抗冲击性方面的相关规范和标准，因此市场上也没有维持混凝土抗震抗冲击性之类的外加剂产品。而工程界也只是采取各种办法来控制或减少这种动载荷对混凝土破坏，比方说“强柱弱梁”、强剪弱弯”、增加抗震结构措施等等。但这些办法都难以确保混凝土在动载荷作用下不开裂或将裂缝控制在无害范围内，不能有效解决混凝土在收到动载荷作用下的开裂现象。传统的混凝土在结硬过程中会发生收缩，温度变化时会发生热胀冷缩现象，导致混凝土产生裂缝，一旦有外力进行施压时就容易断裂，影响建筑需要。
技术实现思路
本专利技术的目的在于，提供一种混凝土抗裂剂，在使用时可增强混凝土构件在地震所产生横向和竖向地震波作用下的抗裂能力，降低地震波对混凝土结构跳动性和摆动性挤压伤害，进而保证建筑物的耐久性。本专利技术的技术方案：一种混凝土抗裂剂，其特征在于，按重量份数计，各组分重量配比如下：8-10份工业无水硫酸铝，10-15份硬石膏，2-5份高强仿钢丝纤维，0.1-0.5份十二烷基硫酸钠，5-10份硅灰，0.5-2份羧甲基纤维素，20-35份硫铝酸盐熟料,5-10份氧化镁，2-5份活性激发剂。前述的一种混凝土抗裂剂，其特征在于，按重量份数计，各组分重量配比如下：9份工业无水硫酸铝，12份硬石膏，3份高强仿钢丝纤维，0.3份十二烷基硫酸钠，7份硅灰，1份羧甲基纤维素，25份硫铝酸盐熟料,8份氧化镁，3份活性激发剂。前述的一种混凝土抗裂剂，其特征在于，按重量份数计，各组分重量配比如下：8份工业无水硫酸铝，10份硬石膏，...
【技术保护点】
1.一种混凝土抗裂剂，其特征在于，按重量份数计，各组分重量配比如下：8‑10份工业无水硫酸铝，10‑15份硬石膏，2‑5份高强仿钢丝纤维，0.1‑0.5份十二烷基硫酸钠，5‑10份硅灰，0.5‑2份羧甲基纤维素，20‑35份硫铝酸盐熟料，5‑10份氧化镁，2‑5份活性激发剂。
【技术特征摘要】
1.一种混凝土抗裂剂，其特征在于，按重量份数计，各组分重量配比如下：8-10份工业无水硫酸铝，10-15份硬石膏，2-5份高强仿钢丝纤维，0.1-0.5份十二烷基硫酸钠，5-10份硅灰，0.5-2份羧甲基纤维素，20-35份硫铝酸盐熟料，5-10份氧化镁，2-5份活性激发剂。2.根据权利要求1所述的一种混凝土抗裂剂，其特征在于，按重量份数计，各组分重量配比如下：9份工业无水硫酸铝，12份硬石膏，3份高强仿钢丝纤维，0.3份十二烷基硫酸钠，7份硅灰，1份羧甲基纤维素，25份硫铝酸盐熟料，8份氧化镁，3份...
【专利技术属性】
技术研发人员：胡汉涛，
申请(专利权)人：湖州五石科技有限公司，
类型：发明
国别省市：浙江,33