一种测定冶金熔渣中Al2O3活度的方法技术

本发明专利技术涉及一种测定冶金熔渣中Al2O3活度的方法，属于冶金冶炼技术领域。本发明专利技术所述方法采用CaF2‑Al2O3作为参考渣，将参考渣与Sn粒、待测渣与Sn粒同时升温，利用高温化学平衡，得到待测渣中Al2O3的活度。本发明专利技术通过采用CaF2‑Al2O3作为参考渣，采用Sn粒作为溶剂，避免了其他方法依靠热力学数据所造成的误差，有效提高了熔渣中Al2O3活度测定的准确性。

A method for the determination of Al2O3 activity in metallurgical slag

The invention relates to a method for determining the activity of Al2O3 in metallurgical slag, which belongs to the metallurgical smelting technology field. The method uses the CaF2 Al2O3 as a reference slag, and the reference slag is heated at the same time with the Sn particles, the slag to be measured and the Sn particles, and the activity of Al2O3 in the residue is obtained by using the high temperature chemical equilibrium. By adopting CaF2 Al2O3 as reference slag and using Sn particles as solvent, the invention avoids the error caused by other methods depending on the thermodynamic data and effectively improves the accuracy of the determination of Al2O3 activity in the slag.

【技术实现步骤摘要】
一种测定冶金熔渣中Al2O3活度的方法
本专利技术涉及一种测定冶金熔渣中Al2O3活度的方法，属于冶金冶炼

技术介绍
冶金熔渣中组元活度作为冶金过程热力学中的重要影响因素之一，一直是冶金热力学领域研究的热点，而Al2O3作为冶金熔渣的典型组元之一，其活度对铁水流动性、炉渣的脱硫能力等有着至关重要的影响。对于熔渣中Al2O3活度的检测，通常采用电动势(EMF)法或化学平衡法，但由于此类方法在测定过程中，常需要借用已知的热力学数据，因此对Al2O3活度检测的精确性造成较大影响，而采用参考渣法因其只使用检测分析的方法测定的元素组成计算相关活度，可有效解决其他方法引用文献数据精度产生的影响。
技术实现思路
本专利技术提供了一种测定冶金熔渣中Al2O3活度的方法，所述方法采用CaF2-Al2O3作为参考渣，将参考渣与Sn粒、待测渣与Sn粒同时升温，利用高温化学平衡，得到待测渣中Al2O3的活度。本专利技术优选为所述参考渣，按质量百分比，由下述组份组成：Al2O330-60％CaF240-70％。本专利技术解决的技术问题为：提供一种测定冶金熔渣中Al2O3活度的方法，由于CaF2-Al2O本文档来自技高网...

【技术保护点】
1.一种测定冶金熔渣中Al2O3活度的方法，其特征在于：所述方法采用CaF2‑Al2O3作为参考渣，将参考渣与Sn粒、待测渣与Sn粒同时升温，利用高温化学平衡，得到待测渣中Al2O3的活度。

【技术特征摘要】
1.一种测定冶金熔渣中Al2O3活度的方法，其特征在于：所述方法采用CaF2-Al2O3作为参考渣，将参考渣与Sn粒、待测渣与Sn粒同时升温，利用高温化学平衡...

【专利技术属性】
技术研发人员：郑海燕，胡心光，沈峰满，姜鑫，高强健，温秋林，郭永春，
申请(专利权)人：东北大学，
类型：发明
国别省市：辽宁,21