The invention discloses a small billet crystallizer protective slag and a preparation method. The slag is composed of MgO 2.7% to 5.4%, CaO 28.6% ~ 36.6%, SiO2 42.5% ~ 46.2%, Al2O3 6.1% to 11%, Fe2O3 2.2% ~ 5.6%, C 4.4% ~ 7.8%. The manufacturing method is made of grass wood ash, cement clinker, fluorite, medium super carbon black and half step strong carbon black as raw material. By stirring and grinding the raw material by stirring the raw material, a spray granulation drying tower is used to make grain and dry, and a kind of small billet mold powder is prepared. The mould slag has strong adsorption capacity, good thermal insulation and good spreading property.
【技术实现步骤摘要】
一种小方坯结晶器保护渣及其制备方法
:本专利技术涉及冶金行业钢水连铸过程中的熔剂,特别涉及一种非预熔型碳钢小方坯结晶器保护渣及其制备方法。
技术介绍
:传统的板坯保护渣为防止分熔一般采用先将原料预熔制成保护渣所需的预熔基料,再进行磨粉、添加熔剂、调炭生产出成品保护渣。这种“造球、预熔、喷雾造粒”空心颗粒保护渣生产线流程长,原料使用较多,管理不易精益化,检验频次多,使用配比方案多,产品生产出错几率大,劳动强度大,成本不易降低。若直接使用矿物原料进行成品保护渣的组织生产,在满足连铸工艺要求的条件下,不仅工序大大缩短,原料管理简单,成本也将大大降低,在相同工艺条件下,非预熔型碳钢保护渣的成本比预熔型保护渣低,产品将有很强的市场竞争优势,因此在激烈的市场竞争下,提高技术质量,降低成本,开发非预熔型碳钢保护渣具有重要意义。
技术实现思路
为克服上述现有技术的不足之处,本专利技术提供一种直接使用矿物原料生产的板坯结晶器保护渣,本专利技术的保护渣,比重小,铺展性好,透气性好,结晶器凹月面处保温效果好,在保证铸坯表面质量的情况下,节省吨钢成本。一种小方坯结晶器保护渣,其组成成分的质量百分比为MgO2.7%~5.4%,CaO28.6%~36.6%,SiO242.5%~46.2%,Al2O36.1%~11%,Fe2O32.2%~5.6%,C4.4%~7.8%。一种小方坯结晶器保护渣的制备方法,以草木灰,水泥熟料,萤石,中超碳黑,半步强炭黑为原料,通过把原料用搅拌磨磨浆后,用喷雾造粒干燥塔造粒干燥,制得一种小方坯结晶器保护渣,本专利技术所述小方坯结晶器保护渣的具体生产方法如下:原料 ...
【技术保护点】
1.一种小方坯结晶器保护渣,其组成成分的质量百分比为MgO 2.7%~5.4%,CaO 28.6%~36.6%,SiO2 42.5%~46.2%,Al2O3 6.1%~11%,Fe2O3 2.2%~5.6%,C 4.4%~7.8%。
【技术特征摘要】
1.一种小方坯结晶器保护渣,其组成成分的质量百分比为MgO2.7%~5.4%,CaO28.6%~36.6%,SiO242.5%~46.2%,Al2O36.1%~11%,Fe2O32.2%~5.6%,C4.4%~7.8%。2.根据...
【专利技术属性】
技术研发人员:不公告发明人,
申请(专利权)人:首臣上海新能源科技有限公司,
类型:发明
国别省市:上海,31