The invention relates to a synthesis method of a reticular Ag/Ag3PO4/AgCl composite photocatalytic material, which is characterized in that the silver net is soaked in a mixed solution of a certain concentration of dilute nitric acid, phosphoric acid and hydrochloric acid in a certain concentration, and the silver net is removed and cleaned with deionized water, and then the network Ag/Ag3PO4/AgCl composite photocatalyst is obtained after the nitrogen is blown to dry. This material can be applied to the fields of photocatalytic gas and liquid organic pollutants degradation. The process is simple and convenient, and it is easy to realize industrial production.
【技术实现步骤摘要】
一种网状Ag/Ag3PO4/AgCl复合光催化材料的合成方法
本专利技术涉及一种网状Ag/Ag3PO4/AgCl复合光催化材料的合成方法，属于无机非金属材料领域。
技术介绍
光催化材料通过吸收光产生空穴-电子对，进而产生活性物种，从而进行光化学反应，主要应用于降解有机污染物、CO2催化还原、水分解制氢等领域。在这种研究背景下，2010年，日本国立物质研究所报道了磷酸银的优越的可见光催化活性，无论是在降解有机污染物和分解水试验中所表现的催化活性，均远高于现有光催剂。随后，研究者围绕磷酸银展开了大量的研究，王韵芳于青岛科技大学学报2017年第38卷第5期的《Ag/Ag3PO4复合材料的制备及可见光催化性能》一文中报道了一种采用葡萄糖做还原剂制备Ag/Ag3PO4复合材料的方法，具体步骤为：将氨水与硝酸银反应形成银铵溶液，加入磷酸钠溶液，将所得沉淀离心分离、洗涤、干燥得到Ag3PO4；将Ag3PO4溶于去离子水后配置悬浮液，加入葡萄糖溶液搅拌，洗涤、干燥后得到Ag/Ag3PO4。申请号为201410147270.5的专利报道了一种磁性磷酸银光催化剂的制备方法，属于光催化...
【技术保护点】
1.一种网状Ag/Ag3PO4/AgCl复合光催化材料的合成方法，其特征在于：将预处理过的银网放入1mol/L的稀硝酸中，于40~50℃浸泡10~30min，取出银网，并氮气吹干；再将银网放入磷酸和盐酸的混合液中，于40~50℃浸泡5~10min，取出银网，用去离子水清洗3~5次，再经氮气吹干后，得到网状Ag/Ag3PO4/AgCl复合光催化材料。
【技术特征摘要】
1.一种网状Ag/Ag3PO4/AgCl复合光催化材料的合成方法，其特征在于：将预处理过的银网放入1mol/L的稀硝酸中，于40~50℃浸泡10~30min，取出银网，并氮气吹干；再将银网放入磷酸和盐酸的混合液中，于40~50℃浸泡5~10min，取出银网，用去离子水清洗3~5次，再经氮气吹干后，得到网状Ag/Ag3PO4/AgCl复合光催化材料。2.如权利要求1所述一种网状Ag/Ag3PO4/AgCl复合光催化材料的合成方法，其特征在于银网中Ag的纯度为99.99%，银网为长方形，长度和宽度均小于500mm，厚度1~2mm，银丝直径为0.1~0.5mm，网孔目数为50~150目...
【专利技术属性】
技术研发人员：李锋锋，张明熹，张利芳，陈晨，郑荣翠，王庆辉，
申请(专利权)人：华北理工大学，
类型：发明
国别省市：河北,13