The invention provides a special foam concrete for external thermal insulation system engineering; it consists of 100 parts of cementitious material, 0~50 parts of admixture, 2~10 parts of polymer polymer, 0.5 to 2 parts of fiber, 2~10 foams and 2~15 admixtures. The invention introduces other components in the ordinary foam concrete to make the special foam concrete have good fluidity, crack resistance, light quality, good affinity with thermal insulation material, high bond strength, adjustable setting time, and also have the function of repairing the wall defect function at the base, and fill it between the insulation board and the wall of the base. It plays the role of bonding and repairing.
【技术实现步骤摘要】
一种用于外墙外保温系统工程的特种泡沫混凝土
本专利技术涉及建筑材料工程领域,具体涉及一种用于外墙外保温系统工程的特种泡沫混凝土。
技术介绍
目前建筑外墙外保温施工技术主要采用粘贴法施工,粘贴法施工受人为因素影响较大,工程质量较难保证,且粘贴法多为点粘或点框粘,使保温系统存在空腔,在风压荷载、气候变化等作用下,保温系统出现了开裂、脱落等现象,影响建筑围护结构热工性能和主体结构安全。
技术实现思路
针对目前建筑外墙外保温系统存在的问题,本专利技术提供一种用于外墙外保温系统工程的特种泡沫混凝土;用于既有建筑外墙外保温系统的维修加固和外墙外保温工程后现浇法施工。本专利技术提供一种用于外墙外保温系统工程的特种泡沫混凝土,由以下重量份数的各组分组成:胶凝材料100份,掺合料10~50份,高分子聚合物2~10份,纤维0.5~2份,发泡剂2~10份,外加剂2~15份。优选地,所述胶凝材料为普通硅酸盐水泥、铝酸盐水泥、石膏、石灰中的一种或几种组成。优选地,所述掺合料为粉煤灰、矿粉、硅灰、石粉中的一种或几种组成。优选地,所述的高分子聚合物为胶粉、乳液、纤维素醚中的一种或几种组成。优选地,所述纤维为聚丙烯纤维、聚乙烯纤维、聚乙烯醇纤维、尼龙纤维、玻璃纤维、碳纤维、氧化铝纤维、碳化硅纤维中的一种或几种组成。优选地,所述发泡剂为松香型发泡剂、动物蛋白发泡剂、植物蛋白发泡剂、表面活性剂中的一种或几种组成。优选地,所述外加剂为减水剂、膨胀剂、促凝剂、早强剂、缓凝剂、降粘剂、激发剂中的一种或几种组成。与现有技术相比,本专利技术具有如下的有益效果:(1)由于纤维的加入,本专利技术材料的抗裂性能 ...
【技术保护点】
1.一种用于外墙外保温系统工程的特种泡沫混凝土,其特征在于,由以下重量份数的各组分组成:胶凝材料100份,掺合料10~50份,高分子聚合物2~10份,纤维0.5~2份,发泡剂2~10份,外加剂2~15份。
【技术特征摘要】
1.一种用于外墙外保温系统工程的特种泡沫混凝土,其特征在于,由以下重量份数的各组分组成:胶凝材料100份,掺合料10~50份,高分子聚合物2~10份,纤维0.5~2份,发泡剂2~10份,外加剂2~15份。2.根据权利要求1所述的用于外墙外保温系统工程的特种泡沫混凝土,其特征在于,所述胶凝材料为普通硅酸盐水泥、铝酸盐水泥、石膏、石灰中的一种或几种组成。3.根据权利要求1所述的用于外墙外保温系统工程的特种泡沫混凝土,其特征在于,所述掺合料为粉煤灰、矿粉、硅灰、石粉中的一种或几种组成。4.根据权利要求1所述的用于外墙外保温系统工程的特种泡沫混凝土,其特征在于,所述的高分子...
【专利技术属性】
技术研发人员:黄沛增,张肖明,程鹏,任普亮,贾忠奎,刘力林,
申请(专利权)人:陕西省建筑科学研究院有限公司,
类型:发明
国别省市:陕西,61