Hydroxy polyacrylic acid resin, isocyanate adduct, polyketone resin, 1, 6 diisocyanate and dumb trimer curing agent are the main film forming substances of this coating. They react with each other and cross link into film; ethyl acetate, n-butyl acetate and cyclohexanone are the main solvent to dissolve the tree fat; 1/16 second nitrocellulose is used in the coating. The viscosity of the coating can be adjusted to facilitate the construction, and the waxy pulp can improve the hand feeling, the fineness and the scratch resistance of the coating, and the high efficiency powder is used to adjust the luminosity of the coating and reduce the light pollution. Various components are reasonable, solvent evaporation rate is reasonable, and has excellent film forming properties. It is a good polyurethane coating.
【技术实现步骤摘要】
一种瓷器聚氨酯漆配方及其制造方法
本专利技术涉及化工涂料制造领域，具体说是一种比较好的双组份瓷器聚氨酯漆的配方及其制造方法。
技术介绍
现在市场上的瓷器聚氨酯漆普遍存在配合复杂、配合后胶化速度快、流平效果不理想等问题，容易导致产生“橘皮”、贝纳德漩涡突出等影响瓷制品涂料最终效果的问题。
技术实现思路
本专利技术提供了一种效果较好的双组份瓷器聚氨酯涂料配方及其制造方法。本专利技术的技术方案是，专利技术了一种优良的双组份瓷器聚氨酯涂料的配方及其制造方法，包括A和B两种组份：A组份：乙酸乙酯、乙酸正丁酯、环己酮、聚酮树脂、1/16秒硝化棉、高效消光粉、羟基聚丙烯酸树脂、不消光蜡浆；B组份：乙酸乙酯、乙酸正丁酯、1，6-己二异氰酸酯、异氰酸酯加成物、哑光三聚体固化剂。组分重量比：A组份：乙酸乙酯15～20%、乙酸正丁酯10～15%、环己酮1～10%、聚酮树脂0.2～2%、1/16秒硝化棉1～10%、高效消光粉1～3%、羟基聚丙烯酸树脂40～60%、不消光蜡浆0.1～2%；B组份：乙酸乙酯20～40%、乙酸正丁酯10～30%、1，6-己二异氰酸酯1～5%、异氰酸酯加成物40～60%、哑光三聚体固化剂5～15%。制造方法：A组份：加入乙酸乙酯、乙酸正丁酯、环己酮、聚酮树脂，搅拌15分钟，加入1/16秒硝化棉，搅拌30分钟，待硝化棉完全溶解后，再加入高效消光粉、羟基聚丙烯酸树脂和不消光蜡浆，继续搅拌30分钟即可；B组份：加入乙酸乙酯、乙酸正丁酯、1，6-己二异氰酸酯、异氰酸酯加成物、哑光三聚体固化剂，搅拌30分钟即可。使用方法：将A组份、B组份和香蕉水按4:1:3的比例混合...
【技术保护点】
1.A组份：乙酸乙酯15千克、乙酸正丁酯15千克、环己酮5千克、聚酮树脂1千克、1/16秒硝化棉5千克、高效消光粉2千克、羟基聚丙烯酸树脂45千克、不消光蜡浆1千克；B组份：乙酸乙酯25千克、乙酸正丁酯20千克、1，6‑己二异氰酸酯5千克、异氰酸酯加成物45千克、哑光三聚体固化剂15千克。
【技术特征摘要】
1.A组份：乙酸乙酯15千克、乙酸正丁酯15千克、环己酮5千克、聚酮树脂1千克、1/16秒硝化棉5千克、高效消光粉2千克、羟基聚丙烯酸树脂45千克、不消光蜡浆1千克；B组份：乙酸乙酯25千...