The invention discloses a cotton fabric anti crease finishing agent, including the following components: 6 citric acid, 8 copies of maleic acid, 6 maleic acid, 8 copies, 20 water borne polyurethane 10, 1 catalyst 3, 3 dispersant 5 copies, 1 dispersant 3, 1 acetate 3, water. The invention has the advantages that the cotton fabric anti crease finishing agent is used in combination with citric acid, maleic acid and waterborne polyurethane, which makes the treated cotton fabric exhibit good crease resistance performance and is still good after several times of water washing; meanwhile, the invention is reduced by adding titanium dioxide in the anti wrinkle agent as a catalyst. The curing temperature in the anti crease finishing process can shorten the curing time, and it can still keep the fabric after the finishing and reduce the free formaldehyde content of the finished fabric under the condition of reducing the anti wrinkle finishing cost.
【技术实现步骤摘要】
一种棉织物抗皱整理剂
本专利技术属于纺织品后整理剂
，具体涉及一种棉织物抗皱整理剂。
技术介绍
棉纤维是种历史悠久的天然纤维，具有很多优良的服用性能，如手感自如、吸湿透气效果好、抗静电、穿着舒适、经济实惠等优点，但纯棉织物也存在弹性差、易起皱、洗后需熨烫等缺点。为了提高织物的抗皱性能，在棉织物整理加工过程中，需要进行抗皱整理。并且随着人们生活水平的提高和生活节奏的加快，人们对服装不仅要求穿着舒适，而且对保持平整外观、料理简便也提出了更高的要求。随着人们对环保和健康意识的增强，人们越来越喜欢穿天然纤维做的衣服，为了克服全棉织物在穿着过程中易起皱，洗后需熨烫的缺陷，棉织物抗皱整理已经成为极其重要的后整理加工工艺。目前，常规的抗皱整理剂在进行织物抗皱整理过程中需要使用的固化温度通常为170℃，固化时间约为1分钟，这将造成一定的电费成本。如何在保障抗皱整理效果的情况下降低织物抗皱整理的成本已经成为亟待解决的问题。
技术实现思路
本专利技术的目的在于针对现有技术的不足，现提供一种固化温度低、抗皱效果好的棉织物抗皱整理剂。为解决上述技术问题，本专利技术采用的技术方案为：一种...
【技术保护点】
1.一种棉织物抗皱整理剂，其特征在于：按重量份计，包括如下组分：柠檬酸6‑8份，马来酸6‑8份，水性聚氨酯10‑20份，催化剂1‑3份，分散剂3‑5份，柔软剂1‑3份，醋酸1‑3份，水90‑120份。
【技术特征摘要】
1.一种棉织物抗皱整理剂，其特征在于：按重量份计，包括如下组分：柠檬酸6-8份，马来酸6-8份，水性聚氨酯10-20份，催化剂1-3份，分散剂3-5份，柔软剂1-3份，醋酸1-3份，水90-120份。2.根据权利要求1所述的一种棉织物抗皱整理剂，其特征在于：所述催...
【专利技术属性】
技术研发人员：仲伟德，
申请(专利权)人：南通香佳纺织科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。