The invention discloses an antibacterial plastic formula, including the following ingredients: 40 polyvinyl chloride, 60 weight portions of polyvinyl chloride, 50 weight portions of acrylic epoxy resin, 15 20 weight hydroxypropyl methyl cellulose, 8 14 weight portions of polyvinyl alcohol, 3 7 weight phr two octyl phthalate, 2 5 weight portion of chitosan, etc. Titanium, 3, 6, weight, boric acid, 1, 5, weight of epoxy soybean oil. The present invention is made of polyvinyl chloride, acrylic epoxy resin, hydroxypropyl methyl cellulose, polyvinyl alcohol, two octyl ester of phthalic two formic acid, chitosan, titanium diboride, boric acid and epoxy soybean oil, each component is interacted and interacted with each other, and the prepared plastic products have good antibacterial properties.
【技术实现步骤摘要】
一种抗菌塑料配方
本专利技术涉及材料
，具体涉及一种抗菌塑料配方。
技术介绍
所谓塑料，其实它是合成树脂中的一种，形状跟天然树脂中的松树脂相似，经过化学手段进行人工合成，而被称之为塑料。塑料是以单体为原料，通过加聚或缩聚反应聚合而成的高分子化合物，俗称塑料或树脂，可以自由改变成分及形体样式。现有的塑料配方很多，但大多不具备抗菌性。
技术实现思路
有鉴于此，本专利技术的目的是提供一种塑料配方，具有良好的抗菌性。本专利技术采取的技术方案是：一种抗菌塑料配方，包括如下原料：40-60重量份聚氯乙烯、30-50重量份丙烯酸环氧树脂、15-20重量份羟丙基甲基纤维素、8-14重量份聚乙烯醇、3-7重量份邻苯二甲酸二辛酯、2-5重量份壳聚糖、1-3重量份二硼化钛、3-6重量份硼酸、1-5重量份环氧大豆油。优选地，所述的羟丙基甲基纤维素为17重量份。优选地，所述的聚乙烯醇为8重量份。优选地，所述的邻苯二甲酸二辛酯为5重量份。优选地，所述的壳聚糖为3重量份。优选地，所述的二硼化钛为2重量份。优选地，所述的硼酸为3.5重量份。优选地，所述的环氧大豆油为2重量份。本专利技术的优点是：本专利技术以聚氯乙烯、丙烯酸环氧树脂、羟丙基甲基纤维素、聚乙烯醇、邻苯二甲酸二辛酯、壳聚糖、二硼化钛、硼酸、环氧大豆油为原料，各个成分相互作用、相互影响，制得的塑料制品具有很好的抗菌性能。具体实施方式为了进一步理解本专利技术，下面结合实施例对本专利技术优选实施方案进行描述，但是应当理解，这些描述只是为进一步说明本专利技术的特征和优点，而不是对本专利技术权利要求的限制。本专利技术实施例公开了一种抗...
【技术保护点】
1.一种抗菌塑料配方，其特征在于包括如下原料：40‑60重量份聚氯乙烯、30‑50重量份丙烯酸环氧树脂、15‑20重量份羟丙基甲基纤维素、8‑14重量份聚乙烯醇、3‑7重量份邻苯二甲酸二辛酯、2‑5重量份壳聚糖、1‑3重量份二硼化钛、3‑6重量份硼酸、1‑5重量份环氧大豆油。
【技术特征摘要】
1.一种抗菌塑料配方，其特征在于包括如下原料：40-60重量份聚氯乙烯、30-50重量份丙烯酸环氧树脂、15-20重量份羟丙基甲基纤维素、8-14重量份聚乙烯醇、3-7重量份邻苯二甲酸二辛酯、2-5重量份壳聚糖、1-3重量份二硼化钛、3-6重量份硼酸、1-5重量份环氧大豆油。2.根据权利要求1所述的抗菌塑料配方，其特征在于所述的羟丙基甲基纤维素为17重量份。3.根据权利要求1所述的抗菌塑料配方，其特征在...
【专利技术属性】
技术研发人员：韦明，杨国威，熊羽，韦煜，
申请(专利权)人：广西超盛网络科技有限责任公司，
类型：发明
国别省市：广西,45
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。