The invention discloses a semi permeable material and its preparation method, which consists of feldspar, limestone, spherical soil, sticky organic powder and barren organic powder. This invention has semi permeable hole stone brick, with glaze layer on the surface of the hole, dense glaze, high strength, wear resistance, and no pollution. Its hole is glazed in a smooth, translucent shape, rich in glaze, clear in texture, and rich in decorative surface. Its texture is designed with marble, and the effect is more realistic and natural. There are few kinds of raw materials, rich resources, low price, simple preparation technology, strong operability, the surface of the products have a mirror surface effect, both the ground and the wall, can be put on a good effect.
【技术实现步骤摘要】
一种半透料洞石干粒及其制备方法
本专利技术属于陶瓷
,具体涉及一种新型干粒及其制备方法,特别涉及一种半透料洞石干粒及其制备方法。
技术介绍
使用半透料洞石干粒烧成得到的半透料洞石砖在色彩,质感以及视觉效果方面能达到天然大理石洞石的逼真效果,装饰效果胜于天然洞石,易于保养,防污性强,其表面凹凸不平的立体面具有独特的装饰效果。随着喷墨技术的普及,半透料洞石干粒结合最新3D喷墨打印技术,洞石纹理可随着设计的变化而变化,搭配自如,可以获得装饰效果更好的半透料洞石砖。技术的发展对半透料洞石干粒提出了新的要求。半透料洞石干粒是干粉干压法制备得到的一种干粒,传统的制作方法为:称料球磨——雾造粒——布料压制成型——烧成这样一个过程,这样制备得到的干粒制品密度较低,烧成时收缩较大,导致最终产品的质量难以控制,不利于使用。开发出一种装饰效果佳,产品性能优异、生产工艺简单的洞石产品,有着重要的市场前景。
技术实现思路
本专利技术的目的在于提供一种用于生产洞石产品的半透料洞石干粒及应用该干粒制备的洞石产品。本专利技术所采取的技术方案是:一种半透料洞石干粒,其原料质量组成为:长石30~45份、石灰石30~50、球土2~10份、粘性有机粉5~50份、瘠性有机粉0~40份。作为上述半透料洞石干粒的进一步改进,粘性有机粉选自面粉、糯米粉或添加有增粘剂的有机物粉末。作为上述半透料洞石干粒的进一步改进,瘠性有机粉的粒径小于80目。作为上述半透料洞石干粒的进一步改进,瘠性有机粉选自木质粉、人造有机质粉。作为上述半透料洞石干粒的进一步改进,干粒的含水量为4~7%。作为上述半透料洞石干粒的进一步 ...
【技术保护点】
1.一种半透料洞石干粒,其原料质量组成为:长石30~45份、石灰石30~50、球土2~10份、粘性有机粉5~50份、瘠性有机粉0~40份。
【技术特征摘要】
1.一种半透料洞石干粒,其原料质量组成为:长石30~45份、石灰石30~50、球土2~10份、粘性有机粉5~50份、瘠性有机粉0~40份。2.根据权利要求1所述的半透料洞石干粒,其特征在于:粘性有机粉选自面粉、糯米粉或添加有增粘剂的有机物粉末。3.根据权利要求1所述的半透料洞石干粒,其特征在于:瘠性有机粉的粒径小于80目。4.根据权利要求1~3任一项所述的半透料洞石干粒,其特征在于:瘠性有机粉选自木质粉、人造有机质粉。5.根据权利要求1~3任一项所...
【专利技术属性】
技术研发人员:曾青蓉,余水林,刘晶,
申请(专利权)人:佛山市道氏科技有限公司,
类型:发明
国别省市:广东,44