The invention discloses an environment-friendly lightweight concrete material. Its raw material includes 100 copies of cement 60, 30 carbon powder of coconut shell, 12 parts of plant straw 5, 2 gypsum powder, 10 plaster powder, 10 carbon powder, 10 portion, 2 zirconia, 6 portion, slag 1, calcite powder, sulphuric acid, sulphuric acid, sulfur Acid zinc 0.1, 0.4, waste rubber particles 2, 6, water 40, 60. The light concrete material of the present invention has the advantages of convenient selection of raw materials, low cost, full use of regenerated resources and reducing environmental pollution, and under the premise of guaranteeing the requirements of hardness, the toughness is excellent, the impact strength is high, and the cutting performance is easy to cut.
【技术实现步骤摘要】
一种环保轻质混凝土材料
本专利技术涉及混凝土
,尤其涉及一种环保轻质混凝土材料。
技术介绍
目前轻质混凝土提倡采用钢渣等工业废料作骨料,但是在广大农村并没有钢渣原料,相反地有大量的稻壳、秸秆等农业废料,这些材料每年只能焚烧处理,不仅浪费,而且还极大地污染环境。曾有过利用稻草作隔热保温混凝土填料的记载,但是因植物纤维易腐败变质,易造成混凝土结构韧性差,抗冲击强度满足不了需求,使用寿命短。
技术实现思路
基于
技术介绍
存在的技术问题,本专利技术提出了一种环保轻质混凝土材料,原材料选用方便,成本极低,能充分利用再生资源和减少环境污染,而且在保证硬度满足要求的前提下,韧性极好,抗冲击强度高,同时具有容易切割的加工性能。本专利技术提出的一种环保轻质混凝土材料,其原料按重量份包括:水泥60-100份,椰壳碳粉30-40份,植物秸秆5-12份,石膏粉2-8份,碳粉4-10份,氧化锆2-6份,钢渣1-5份,河沙2-8份,方解石粉1-5份,沉淀硫酸钡1-3份,硫酸锌0.1-0.4份,废弃橡胶颗粒2-6份,水40-60份。优选地,水泥、椰壳碳粉、植物秸秆的重量比为80-90:33-37:8-10。优选地,石膏粉、碳粉、氧化锆的重量比为4-6:6-8:3-5。优选地,钢渣、河沙、方解石粉的重量比为2-4:4-6:2-4。优选地,沉淀硫酸钡、硫酸锌、废弃橡胶颗粒的重量比为1.5-2.5:0.2-0.3:3-5。本专利技术所得混凝土只需按照上述配方充分混合,然后按照一般混凝土的养护方法正常养护10-15天即可。本专利技术采用水泥为主料,采用椰壳碳粉、植物秸秆代替部分水泥,可有效降低 ...
【技术保护点】
1.一种环保轻质混凝土材料,其特征在于,其原料按重量份包括:水泥60‑100份,椰壳碳粉30‑40份,植物秸秆5‑12份,石膏粉2‑8份,碳粉4‑10份,氧化锆2‑6份,钢渣1‑5份,河沙2‑8份,方解石粉1‑5份,沉淀硫酸钡1‑3份,硫酸锌0.1‑0.4份,废弃橡胶颗粒2‑6份,水40‑60份。
【技术特征摘要】
1.一种环保轻质混凝土材料,其特征在于,其原料按重量份包括:水泥60-100份,椰壳碳粉30-40份,植物秸秆5-12份,石膏粉2-8份,碳粉4-10份,氧化锆2-6份,钢渣1-5份,河沙2-8份,方解石粉1-5份,沉淀硫酸钡1-3份,硫酸锌0.1-0.4份,废弃橡胶颗粒2-6份,水40-60份。2.根据权利要求1所述环保轻质混凝土材料,其特征在于,水泥、椰壳碳粉、植物秸秆的重量比为...
【专利技术属性】
技术研发人员:贾军,
申请(专利权)人:蚌埠市宝运商品混凝土有限公司,
类型:发明
国别省市:安徽,34