The invention discloses a magnesium phosphate cement, including a component of the following mass: a Magnesium Oxide mixture 45~75 portion, a dihydrogen phosphate 15~50 portion and a retarder 2~10, wherein the Magnesium Oxide mixture includes calcined dolomite powder, and the preparation method of the calcined dolomite powder is that the pulverized dolomite is mixed with the silicon component. After calcining at 1100~1800 C and grinding the calcined product, the calcined dolomite powder is obtained. Compared with the traditional magnesium phosphate cement, the magnesium phosphate cement prepared by the invention has similar performance and white color, at the same time, it expands the range of the selection of Magnesium Oxide raw material in magnesium phosphate cement, significantly reduces the cost of magnesium phosphate cement, and has a good market prospect.
【技术实现步骤摘要】
一种磷酸镁水泥
本专利技术属于建筑材料领域，尤其涉及磷酸镁水泥。
技术介绍
磷酸镁水泥具有早强快硬、粘结强度高及体积稳定性好等优异性能，已在混凝土结构快速修补与加固等领域得到良好应用，同时在生物假体、危险废物的固化处理等方面也展现出广泛的应用前景。磷酸镁水泥是由重烧氧化镁、磷酸盐及缓凝剂等按一定比例配制而成。其中，重烧氧化镁在磷酸镁水泥中的占比可达50-80％，它主要是由菱镁矿经1600℃以上高温煅烧后磨细而得，其品质对磷酸镁水泥性能有着至关重要的影响。目前，我国已探明的菱镁矿矿区主要分布在辽宁、山东等地，来源和储量有限，因此煅烧后得到的氧化镁价格偏高，不利于磷酸镁水泥的应用和推广。除菱镁矿矿外，白云石[CaMg(CO3)2]是自然界中另一种储量更为丰富的镁矿资源。我国各地已勘明的矿区多达208处，保有储量为82.2亿吨，各矿床多已开发利用。在全国范围内白云石的分布比菱镁矿更广，储量更为丰富。若将白云石中的氧化镁应用于磷酸镁水泥的制备，可显著扩大磷酸镁水泥原材料中氧化镁原材料的选择范围。虽然白云石含有较多MgO，却不能通过直接煅烧后应用于磷酸镁水泥的制备。当白云石...
【技术保护点】
1.一种磷酸镁水泥，其特征在于，包括以下质量份的组分：氧化镁混合物45~75份，磷酸二氢盐15~50份，缓凝剂0~10份；其中，所述氧化镁混合物包括煅烧白云石粉，所述煅烧白云石粉的制备方法为：将粉碎的白云石与含硅组分混合均匀后于1100~1800℃煅烧，再将煅烧产物粉磨后，即得到所述的煅烧白云石粉。
【技术特征摘要】
1.一种磷酸镁水泥，其特征在于，包括以下质量份的组分：氧化镁混合物45~75份，磷酸二氢盐15~50份，缓凝剂0~10份；其中，所述氧化镁混合物包括煅烧白云石粉，所述煅烧白云石粉的制备方法为：将粉碎的白云石与含硅组分混合均匀后于1100~1800℃煅烧，再将煅烧产物粉磨后，即得到所述的煅烧白云石粉。2.根据权利要求1所述的磷酸镁水泥，其特征在于，所述含硅组分的SiO2含量在50%以上。3.根据权利要求1所述的磷酸镁水泥，其特征在于，所述含硅组分为硅石粉、硅灰、硅藻土和黏土中的至少一种。4.根据权利要求2所述的磷酸镁水泥，其特征在于，所述含硅组分与白云石的质量比...
【专利技术属性】
技术研发人员：钱觉时，余金城，唐江昱，秦继辉，岳燕飞，范英儒，尤超，
申请(专利权)人：重庆大学，
类型：发明
国别省市：重庆,50