The present invention discloses a film transfer ink and its preparation method, including the following weight components: 18~20 portion of vinyl chloride vinyl acetate copolymer, 20~22 portion of polyaldehyde resin, 20~22 portion of ethylene glycol ether acetate, 15~25 portion of edible alcohol, 12~30 portion of titanium dioxide, 3~5 portion of demoulding agent, and 0.3~0.5 portion of leveling agent. Compared with the preparation methods of the existing technology, the film transfer ink of the invention has the following beneficial effects: 1) the vinyl chloride vinyl acetate copolymer is selected as the connecting material, and the polyaldehyde resin with good alcohol solubility is added, and the original must be dissolved in the resin with toluene, xylene and acetone as the solvent; and 2) addition of demoulding is added. The agent improves the specific transfer performance of the ink.
【技术实现步骤摘要】
一种薄膜转移油墨及其制备方法
本专利技术涉及中药保健领域，具体涉及一种薄膜转移油墨及其制备方法。
技术介绍
目前国内市场上使用的PVC薄膜转移油墨，都会用二甲苯、甲苯、丙酮和环己酮等有毒有害溶剂，对环境及生产工人的身体健康有严重伤害。甲苯、二甲苯色生产多从煤焦油或石油裂解产生，在工业上主要用于油漆、涂料、胶水的有机溶剂，也可制造糖精、燃料、药物和炸药等。生产中甲苯主要通过呼吸系统、皮肤吸入人体，对皮肤、黏膜有刺激性，对中枢神经系统有麻醉作用，对人体有极大的伤害。中国专利技术专利申请CN201010269390.4，公开了涉及油墨组合物。本专利技术提供含有金属颜料的油墨组合物，其具有优异的油墨排出稳定性和印字稳定性。所述油墨组合物含有有机溶剂、金属颜料和树脂，其特征在于，相对于上述油墨组合物的总量，上述有机溶剂含有60质量％以上的二乙二醇二乙醚、24～37质量％的γ-丁内酯和/或四乙二醇二甲醚、和大于1质量％且小于5质量％的四乙二醇单丁醚，上述金属颜料通过光散射法测得且换算成球体而得到的50％平均粒径为0.8～1.2μm。综上所述，现有的转移油墨中的溶剂含有有毒的溶...
【技术保护点】
1.一种薄膜转移油墨，其特征在于：包括如下重量份的组分：氯乙烯‑醋酸乙烯共聚物 18~20份，聚醛树脂 20~22份，乙二醇乙醚醋酸酯 20~22份，食用酒精 15~25份，钛白粉 12~30份，脱模剂 3~5份，流平剂 0.3~0.5份，所述脱模剂为聚乙烯蜡浆，所述流平剂为聚醚二甲基硅烷改性剂。
【技术特征摘要】
1.一种薄膜转移油墨，其特征在于：包括如下重量份的组分：氯乙烯-醋酸乙烯共聚物18~20份，聚醛树脂20~22份，乙二醇乙醚醋酸酯20~22份，食用酒精15~25份，钛白粉12~30份，脱模剂3~5份，流平剂0.3~0.5份，所述脱模剂为聚乙烯蜡浆，所述流平剂为聚醚二甲基硅烷改性剂。2.根据权利要求1所述的薄膜转移油墨，其特征在于：所述氯乙烯-醋酸乙烯共聚物为18份，所述聚醛树脂为22份，所述乙二醇乙醚醋酸酯为22份，所述食用酒精为20份，所述钛白粉为16份，所述脱模剂为4.5份，所述...
【专利技术属性】
技术研发人员：蒋加寿，周定兴，
申请(专利权)人：嘉兴凯兴达新材料科技有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。