Compound water treatment agent suitable for valve cooling system of converter station

The invention discloses a compound water treatment agent suitable for valve cooling system of converter station. In view of the corrosion on the surface of the aluminum radiator on the converter station, the invention provides a compound water treatment agent, which is divided into three groups according to the mass percentage: 30 tryptophan, 15, 35%, 2, mercapthiazole, 15, 8 35%, 8 nitroquinoline. The components of the compound water treatment agent are organic reagents, green no pollution, low quantity and high efficiency, and improved the single and low efficiency situation of the corrosion inhibitor of aluminum in the valve cold system at the present stage. One

【技术实现步骤摘要】
适用于换流站阀冷系统的复合型水处理剂
本专利技术属于水处理剂领域，具体地说是一种适用于换流站阀冷系统的复合型水处理剂。
技术介绍
电力行业中高压直流输电技术是目前世界上先进的节能输变电技术之一，换流站是高压直流输电系统中转换交流与直流并满足电力系统安全稳定运行要求的站点，换流阀是换流站核心设备之一。晶闸管换流阀在换流站中承担交流-直流转换功能，换流阀正常运行时，晶闸管通过大电流，会散发大量的热，导致可控硅温度急剧上升，如果不对可控硅进行有效冷却，可控硅将被烧坏，直接影响到直流输电的安全性和可靠性，甚至造成直流输电系统停运，因此需要对换流阀系统进行冷却来确保其正常工作，因而换流阀冷却系统是直流输电系统中最重要的辅助系统。由于阀冷水中树脂粉末、溶解氧、电解电流等环境影响，阀冷系统内的换流阀元件易发生腐蚀问题，特别是铝制散热器尤为严重，散热片的腐蚀及腐蚀后的沉积给直流系统稳定性带来了巨大的危害，已多次引发直流输电系统故障，因此需要对水路系统腐蚀开展定量和系统的研究，尤其是内冷系统铝散热片腐蚀防护问题。目前，阀冷系统中所使用的水处理剂品种比较单一，较为常用的是乙二醇，但是实际所起的缓蚀效果并本文档来自技高网...

【技术保护点】
1.适用于换流站阀冷系统的复合型水处理剂，其特征在于，按质量百分数计的各组分

【技术特征摘要】
1.适用于换流站阀冷系统的复合型水处理剂，其特征在于，按质量百分数计的各组分为：30-60％的色氨酸，15-35％的6-氨基-2-巯基苯并噻唑，15-35％的8-硝基喹啉。2.根据权利要求1所述的适用于换流站阀冷系统的复合型水处理剂，其特征在于，所述色氨酸的质量百分数为40-50％。3.根据权利要求1所述的适用于换流站阀冷系统的复合型水处理剂，其特征在于，所述6-氨基-2-巯基苯并噻唑的质量百分数为20-30％。4.根据权利要求3所述的适用于换流站阀冷系统的复合型水...