The invention discloses an anti ultraviolet radiation women's clothing and its processing technology. The processing technology includes: (1) preparing anti ultraviolet finishing liquid: mixing tea branch citrus peel pectin extract and water in accordance with the mass ratio of 5: (95, 105) and stirring 40 minutes for 90 minutes, getting anti UV finishing liquid; (2) fabric finishing: the fabric is completely immersed in anti UV. The finishing liquid was arranged 30 minutes for 60 minutes, and the bath ratio was 1: (30). The fabric after finishing was rolled and dried to get anti ultraviolet radiation fabric. The fabric was tailored to get anti UV radiation women's clothing. The invention provides a kind of anti ultraviolet radiation women's wear, creative use of tea branch citrus peel extract as anti UV finishing agent to prevent the penetration of ultraviolet rays. It can prevent the damage caused by ultraviolet radiation to the human body. It can also make use of ultraviolet radiation to heat the heat. It has the effect of keeping warm, improving the microcirculation of human body and enhancing the cell. The anti ultraviolet radiation fabric of the invention has high comfort, flexibility, elasticity and good service performance. One
【技术实现步骤摘要】
抗紫外辐射女装及其加工工艺
本专利技术涉及一种具有抗紫外辐射功能的女装。
技术介绍
紫外线可使天然纤维与合成纤维的韧性、强度等力学性能下降，纤维的抗紫外改性已成为重要的研究方向。抗紫外改性，即采用抗紫外助剂对纤维、纱线或织物进行改性，从而达到吸收或反射紫外线的目的。不同种类的纤维织成的织物，其抗紫外的能力不同。在众多的纺织纤维中，棉和粘胶纤维的紫外线透过率较高，抗紫外性能较差。羊毛、蚕丝等蛋白质纤维的分子结构中含有芳香族氨基酸，具有较高的紫外线吸收能力，对300nm以下的紫外线有强烈吸收。涤纶由于含有芳香环结构，同样具有较高的紫外线吸收能力。锦纶相当容易透过紫外线。腈纶由于氰基之间的偶极作用，抗紫外线能力较差。一般来说，天然纤维和常规纤维制品尚达不到保护人体免受紫外线伤害的保健要求。同为棉织物，抗紫外性能也可能不同，影响因素有织物的组织结构、织物的颜色和后整理加工等。紫外线照射到织物上，一部分被吸收，一部分被反射，一部分透过织物。一般情况下，紫外线的透过率+反射率+吸收率＝100％。因此，吸收率和反射率越高，透过率就降低，防护性能就越好。抗紫外线整理剂就是通过吸收或反射紫外线来达到紫外防护效果的。目前，对紫外线防护服装及产品推荐应用的指标主要有：紫外线防护系数(UPF)和紫外线透过率T(UVA)，T(UVB)。紫外线防护系数表示织物防护紫外线的能力，它是紫外线对未防护的皮肽的平均辐射量与要经测试的织物遮挡后紫外线辐射量的比值。随着物质生活水平的提高以及科学技术的发展，人们对纺织品的要求不再局限于保暖、舒适等原有的基本特性。根据纺织品的不同用途，人们还希望其...
【技术保护点】
1.一种抗紫外辐射女装的加工工艺，其特征在于，包括下述步骤：
【技术特征摘要】
1.一种抗紫外辐射女装的加工工艺，其特征在于，包括下述步骤：(1)配制抗紫外整理液：将茶枝柑皮果胶提取物与水按照质量比为5：(95-105)混合后在温度为30-50℃、以100-300转/分钟的转速搅拌40-90分钟，得到抗紫外整理液；(2)面料整理：将面料完全浸入温度为30-50℃的抗紫外整理液中整理30-60分钟，浴比为1:(30-80)，将整理后的面料轧液后在80-95℃烘10-30分钟，在110-145℃烘1-6分钟，得到抗紫外辐射面料，将抗紫外辐射面料按常规工艺剪裁缝制，得到抗紫外辐射女装。2.一种抗紫外辐射女装的加工工艺，其特征在于，包括以下步骤：(1)制备茶枝柑皮果胶提取物：将茶枝柑皮粉碎后过20-50目筛，得茶枝柑皮粉末，将2.75-5.25Kg茶枝柑皮粉末加入到30.5-41.2L乙醇中，在60-90℃水浴加热回流2.5-6.5小时后，冷却至30-35℃，过滤，所得滤渣在42-55℃干燥12-24小时，将干燥后的滤渣与pH值为1-3的酸液按照用量比为1g:(25-55)mL的比例混合后在65-95℃水浴加热100-150分钟，然后冷却至30-35℃，过滤，将滤液蒸发浓缩得到浓缩液，所述浓缩液质量为过滤所得滤液质量的1/3-1/2,然后向浓缩液中加入质量为浓缩液质量2.5-4.5倍的乙醇，在3-5℃保存12-18小时，过滤，所得滤渣用500-1000g水冲洗后在45-65℃干燥12-24小时，得到茶枝柑皮果胶提取物；(2)配制抗紫外整理液：将茶枝柑皮果胶提取物与水按照质量比为5：(95-105)混合后在温度为30-50℃、以100-300转/分钟的转速搅拌40-90分钟，得到抗紫外整理液；(3)面料整理：将面料完全浸入温度为30-50℃的抗紫外整理液中整理30-60分钟，浴比为1:(30-80)，将整理后的面料轧液后在80-95℃烘10-30分钟，在110-145℃烘1-6分钟，得到抗紫外辐射面料，将抗紫外辐射面料按常规工艺剪裁缝制，得到抗紫外辐射女装。3.一种抗紫外辐射女装的加工工艺，其特征在于，包括以下步骤：(1)制备茶枝柑皮果胶提取物：将茶枝柑皮粉碎后过20-50目筛，得茶枝柑皮粉末，将2.75-5.25Kg茶枝柑皮粉末加入到30.5-41.2L乙醇中，在60-90℃水浴加热回流2.5-6.5小时后，冷却至30-35℃，过滤，所得滤渣在42-55℃干燥12-24小时，将干燥后的滤渣与pH值为1-3的酸液按照用量比为1g:(25-55)mL的比例混合后在65-95℃水浴加热100-150分钟，然后冷却至30-35℃，过滤，将滤液蒸发浓缩得到浓缩液，所述浓缩液质量为过滤所得滤液质量的1/3-1/2,然后向浓缩液中加入质量为浓缩液质量2.5-4.5倍的乙醇，在3-5℃保存12-18小时，过滤，所得滤渣用500-1000g水冲洗后在45-65℃干燥12-24小时，得到茶枝柑皮果胶提取物；(2)配制抗紫外整理液：将茶枝柑皮果胶提取物与水按照质量比为5：(95-105)混合后在温度为30-50℃、以100-300转/分钟的转速搅拌40-90分钟，加入质量为茶枝柑皮果胶提取物质量15-45倍的膨润土-氧化钛复合物，在温度为30-50℃、以100-300转/分钟的转速搅拌40-60分钟，得到抗紫外整理液；所述膨润土-氧化钛复合物的制备方法如下：S1：将20-30mL乙醇、10-20mL钛酸四丁酯、2-5mL冰醋酸混合均匀，得到混合物A，将2-5mL浓度为1mol/L的硝酸水溶液和5-15ml乙醇混合均匀，得到混合物B，将全部的混合物B加入到混合物A中，加入的同时进行搅拌，搅拌的转速为450-600转/分钟、温度为25-35℃，全部加完后继续在25-35℃、以450-600转/分钟的转速搅拌15-25分钟，得到钛溶胶；S2：将0.5-2.5g钠基膨润土与80-110g水混合均匀，在25-40℃、以200-400转/分钟的转速搅拌3.5-7小时，得到钠基膨润土悬浮液，将钠基膨润土悬浮液在2...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。