The present invention discloses a method of rust removing and rust prevention for post pouring steel bar. The main point of the technical scheme is to spray the cement paste with steel bar inhibitor to the post poured steel bar, knock the steel bar before pouring the reinforced concrete in the post pouring strip, knock out the cemented block which has not been stuck, and then unify the concrete. After the use of the invention, the post cast steel bar can effectively prevent rust, even if the rebar has been corroded and corroded seriously, the invention can effectively remove rust stains and rust residue, and solve the technical blank of the rust removing method which is not suitable for the post cast steel bar in the construction field.
【技术实现步骤摘要】
后浇带钢筋除锈防锈方法
本专利技术涉及钢筋除锈防锈方法，尤其涉及已绑扎的后浇带钢筋除锈防锈方法。
技术介绍
现在建筑中后浇带钢筋都是在建筑物主体完工后再进行除锈、浇筑混凝土作业。但是在现实中即便是主体建筑顺利完工，后浇带钢筋也会裸露在空气中锈蚀两三年。后浇带钢筋因没有合适的防锈方法故基本上都不采取防护措施，待后浇带钢筋浇筑混凝土时已经锈蚀很严重。后浇带钢筋因没有合适的、有效的除锈工具、除锈方法，导致后浇带钢筋在浇筑混凝土时不除锈或简单的、象征性的除下锈，相当于没除锈。1990年《东北水利水电》出版一篇《钢筋表面预涂水泥浆后再浇筑混凝土对其握裹力增强的机理初探》，文中明确阐述了钢筋在预涂水泥浆后能有效增强钢筋混凝土的握裹力。
技术实现思路
本专利技术解决的技术问题就是后浇带钢筋除锈防锈方法，一种后浇带钢筋有效防锈、锈蚀钢筋能有效除锈的方法，其特征包括如下步骤：（1）在水泥浆中添加钢筋阻锈剂，并搅拌均匀；（2）使用专用喷浆机把加有钢筋阻锈剂的水泥浆喷涂到钢筋表面；（3）使用高压喷涂机把钢筋除锈剂均匀的喷涂到螺纹钢表面；（4）后浇带钢筋在浇筑混凝土时先敲打后浇带钢筋，敲打掉粘结不牢的水泥块，粘结牢固的水泥块不必再清理；（5）敲打后的后浇带钢筋统一浇筑混凝土；进一步的，所述步骤（1）中的钢筋阻锈剂为郑州三超除锈技术有限公司生产的钢筋阻锈剂；进一步的，所述步骤（2）中的喷浆机为高压喷涂机；本专利技术明显的效果为：后浇带钢筋使用本专利技术能强效防锈，即便是已发生锈蚀、锈蚀严重的后浇带钢筋使用本专利技术能有效的去除锈渍、锈渣，解决目前建筑领域中后浇带钢筋没有适合除锈方法的技...
【技术保护点】
后浇带钢筋除锈防锈方法，其特征在于，包括以下步骤：(1)在水泥浆中添加钢筋阻锈剂，并搅拌均匀；(2)使用专用的喷浆机把加有钢筋阻锈剂的水泥浆喷涂到钢筋表面；(3)后浇带钢筋浇筑混凝土时先敲打后浇带钢筋，敲打掉粘结不牢的水泥块，粘结牢固的水泥块不必再清理；(4)敲打后的后浇带钢筋统一浇筑混凝土。
【技术特征摘要】
1.后浇带钢筋除锈防锈方法，其特征在于，包括以下步骤：(1)在水泥浆中添加钢筋阻锈剂，并搅拌均匀；(2)使用专用的喷浆机把加有钢筋阻锈剂的水泥浆喷涂到钢筋表面；(3)后浇带钢筋浇筑混凝土时先敲打后浇带钢筋，敲打掉粘结不牢的水泥块，粘结牢固的水泥块不必再清理；(4)敲...
【专利技术属性】
技术研发人员：李春山，刘向阳，赵阳，李春喜，李春超，
申请(专利权)人：郑州三超除锈技术有限公司，李春山，刘向阳，
类型：发明
国别省市：河南,41