The purpose of the invention is to provide a polypropylene special antibacterial masterbatch for improving the antibacterial property of polypropylene masterbatch and a preparation method thereof. Polypropylene (PP) is a non polar crystalline plastic. It is one of the five general-purpose plastics. It is very versatile for its rich materials, cheap price, easy processing and so on. Polypropylene is commonly used as a polymer material in packaging of food and hygiene products. Therefore, it is an inevitable trend to study polypropylene antibacterial. The antibacterial polypropylene special masterbatch can overcome the deficiency of the original polypropylene pollution, and is of great significance for the application and further promotion of polypropylene material. The hygienic coefficient of food and sanitary products packaging is also improved.
【技术实现步骤摘要】
聚丙烯抗菌母料
本专利技术属聚丙烯材料生产
,具体说是一种改善聚丙烯原有不足，使其具有抗菌性能的聚丙烯抗菌专用母料及其制备方法。
技术介绍
聚丙烯，英文名称：Polypropylene,缩写名称PP。其化学式为：(C3H6)N。结构式如下所示：聚丙烯(PP)为非极性的结晶塑料，是五大类通用塑料之一，原料来料丰富、价格便宜、易于加工成型等等，因此用途非常广泛。聚丙烯作为食品和卫生用品包装中常用高分子材料，因此对聚丙烯进行抗菌的研究是必然的趋势。
技术实现思路
本专利技术的目的是提供一种改善聚丙烯母料抗菌性的聚丙烯抗菌专用母料及其制备方法。聚丙烯抗菌专用母料由下列重量比原料组成：聚丙烯原料：80～120氧化聚乙烯分散剂：4.0～8.0载银沸石抗菌剂：70.0～90.0玻璃粉抗菌剂：15.0～25.0硬脂酸润滑剂：3.0～5.0该聚丙烯抗菌专用母料的制备方法，包括下列步骤：先将上述各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为90-100℃，二区为150-180℃，三区为200-210℃，四区为200-205℃；五区为190-200℃，停留时间为1-2分钟，压力为10-15Mpa。本专利技术所得聚丙烯抗菌专用母料的力学性能能够达到使用标准，并且能够极大提高聚丙烯材料的抗菌性能，使聚丙烯材料在使用时提高安全性能。具体实施方式下面通过具体实施方式对本专利技术做进一步的说明，以下实施例仅是对本专利技术进行说明而非对其加以限定。实施例1：(1)按重量比分分别称取各原料如下：聚丙烯原料：100...
【技术保护点】
聚丙烯抗菌母料，其特征在于：由下列重量比原料组成，聚丙烯原料：80～120氧化聚乙烯分散剂：4.0～8.0载银沸石抗菌剂：70.0～90.0玻璃粉抗菌剂：15.0～25.0硬脂酸润滑剂：3.0～5.0。
【技术特征摘要】
1.聚丙烯抗菌母料，其特征在于：由下列重量比原料组成，聚丙烯原料：80～120氧化聚乙烯分散剂：4.0～8.0载银沸石抗菌剂：70.0～90.0玻璃粉抗菌剂：15.0～25.0硬脂酸润滑剂：3.0～5.0。2.根据权利要求1所述的聚丙烯抗菌母料，其特征在于：最优重量比原料组成为：聚丙烯原料：100氧化聚乙烯分散剂：6.0载银沸石抗菌剂：80.0玻璃粉抗菌剂：20.0硬脂酸润滑剂：4.0。3.根据权利要求1所述的聚丙烯抗菌母料，...
【专利技术属性】
技术研发人员：丁磊，
申请(专利权)人：青岛绿谷生物科技有限公司，
类型：发明
国别省市：山东,37