A method for improving the formability of graphitized steel sheet belongs to the technical field of iron and steel material processing. It is characterized by the temperature deformation of graphitized graphitized steel after graphitization, which is used to improve the formability of the graphitized sheet by controlling the refinement and homogenization of the dynamic grain of ferrite. The concrete method is to heat the graphitized steel plate through the graphitization to 550~710 C, and then make the roll rolling of 8 to 15% after the uniform temperature, and the air cooling to room temperature after rolling. The graphitized steel plate treated by this method can refine and uniform the ferrite grain, and the forming property is good, the ratio of flexion to strength is less than 0.56, the strain hardening exponent is more than 0.25, and the plane anisotropy is less than 0.15.
【技术实现步骤摘要】
一种提高石墨化钢板冲压成形性能的方法
本专利技术涉及一种提高石墨化钢板冲压成形性能的方法，属于钢铁材料加工
技术介绍
石墨化钢板的制备流程主要是包括炼钢、浇注、热轧或冷轧、石墨化处理等工艺过程。其中，钢板经石墨化处理后，表现出较高的冲压成形性能，具有较低的屈强比，能够软化到与低碳钢一样的水平。经石墨化处理的钢板，其组织主要由铁素体+石墨组成。然而，由于石墨化处理过程需要的时间较长，往往导致钢板中的铁素体组织粗大，且不均匀，这样的组织特点，很难使钢板具有良好的冲压成形性能。因此，为解决现有石墨化处理方法中存在的铁素体晶粒粗大，且不均匀的问题，本专利技术提出了利用温变形技术，对石墨化处理后的石墨化钢板进行铁素体动态再结晶的温轧，以实现铁素体晶粒的细化、均匀化，为后续冲压成形提供良好的预备组织，以进一步提高其冲压成形性能。
技术实现思路
经石墨化处理后的石墨化钢板，具有较高的冲压成形性能。由于石墨化处理过程中易造成铁素体晶粒粗大，且不均匀。因此，为了解决这一问题，本专利技术基于温变形可使铁素体再结晶，来使铁素体晶粒细化和均匀化，提出了一种可进一步提高石墨化钢板冲压...
【技术保护点】
一种提高石墨化钢板冲压成形性能的方法，其特征在于利用温变形技术，对石墨化处理后的石墨化钢板进行铁素体动态再结晶的温变形，以实现铁素体晶粒的细化和均匀化；具体方法是将经过石墨化处理的石墨化钢板加热到550～710℃，待均温后进行压下量为8～15％的平辊轧制，轧后空冷至室温。
【技术特征摘要】
1.一种提高石墨化钢板冲压成形性能的方法，其特征在于利用温变形技术，对石墨化处理后的石墨化钢板进行铁素体动态再结晶的温变形，以实现铁素体晶粒的细化和均匀化；具体方法是将经过石墨化处理的石墨化钢板加热到550～710℃，待均温后进行压下量为8～15％的平辊轧制，轧后空冷至室温。2.据权利要求1所述的一种提高石墨化钢板冲压成形性能的方法，其特征在于，所述的石墨化处...
【专利技术属性】
技术研发人员：张永军，张鹏程，王九花，于文杰，韩静涛，
申请(专利权)人：北京科技大学，
类型：发明
国别省市：北京,11