The invention provides a wear-resistant clear face paint for a waterborne double component large class table and a preparation method. The wood coating includes two components of a component and a second component. The fraction weight percentage is divided into 70% to 80%, 0.1% to 1% of defoamer, 0 to 1%, 0.1% to 1%, and a thickening agent, and a film forming aid. The agent is 1% ~ 5%, wetting agent 0.1% ~ 0.5%, glass powder 2% ~ 5%, anti settling agent 1% ~ 3%, PH regulator 0.1% ~ 0.3%, water 5% ~ 5%. The waterborne double component large class table has the following advantages: water dilution, low VOC volatilization, constant temperature curing and fine finish of the film. Besides good physical and chemical properties, it has excellent wear resistance and delimit resistance.
【技术实现步骤摘要】
水性双组分大班台面用耐磨清面漆及其生产方法
本专利技术涉及一种水性双组分木器涂料，特指一种在水可分散型聚异氰酸酯参与反应固化的双组分水性木器涂料及其生产方法，该涂料可用于办公桌面班台面的施工，保证使用过程中耐磨、抗划伤性能。
技术介绍
环保涂装趋于水性漆行业的潮流式驱使，针对目前市场和消费的需求热度，社会环保理念的推进，水性漆成为水漆产业未来发展的必然趋势。目前水性漆从功能上还不能完全代替油性漆，主要体现在丰满度、硬度、耐磨、抗划、耐化学品性能等方面。目前市场上水性漆的主流是水性单组分产品，漆膜干薄、偏软，不耐磨，还不能满足高档的办公家具特别是大班台面的需求。本专利技术研发成功了水性双组分大班台面用耐磨清面漆，通过选用含羟基的水性丙烯酸分散体与水性异氰酸酯的反应交联，提高了涂膜的物化性能，再通过添加玻璃粉，制成抗划耐磨高透的水性双组分清面漆。
技术实现思路
本专利技术的目的是提供一种水性双组分大班台面用耐磨清面漆及其生产方法，用于办公桌面的水性化涂装。本专利技术所说的水性双组分大班台面用耐磨清面漆，包括甲组分和乙两个组分，甲组分重量百分比组分为：上述各个组分的百分比之...
【技术保护点】
水性双组分大班台面用耐磨清面漆，其特征在于，包括甲和乙两个组分，甲组分重量百分比组分为：水性羟基丙烯酸分散体 70%～80%，消泡剂 0.1%～1%，消光剂 0～1%，增稠剂 0.1%～1%，成膜助剂 1%～5%，润湿剂 0.1%～0.5%，玻璃粉 2%～5%，防沉剂 ...
【技术特征摘要】
1.水性双组分大班台面用耐磨清面漆，其特征在于，包括甲和乙两个组分，甲组分重量百分比组分为：水性羟基丙烯酸分散体70%～80%，消泡剂0.1%～1%，消光剂0～1%，增稠剂0.1%～1%，成膜助剂1%～5%，润湿剂0.1%～0.5%，玻璃粉2%～5%，防沉剂1%～3%，PH调节剂0.1%～0.3%，水5%～15%，上述各个组分的百分比之和为100%；乙组分为水可分散型聚异氰酸酯固化剂，使用丙二醇甲醚醋酸酯兑稀降低粘度，固含为80%。2.根据权利要求1所述的水性双组分大班台面用耐磨清面漆，其特征在于，所述的水性树脂（水性羟基丙烯酸分散体）含-OH基水性丙烯酸酯分散体。3.根据权利要求1所述的水性双组分大班台面用耐磨清面漆，其特征在于，所述消泡剂为聚硅氧烷-聚醚共聚物，所述消光剂为气相二氧化硅类型，所述增稠剂为缔合型聚氨酯增稠剂中的...
【专利技术属性】
技术研发人员：徐芬，周巍，
申请(专利权)人：上海展辰涂料有限公司，展辰新材料集团股份有限公司，北京展辰新材料有限公司，青岛展辰新材料有限公司，成都展辰涂料有限公司，福州展辰新材料有限公司，
类型：发明
国别省市：上海,31