本发明专利技术公开了一种水性氧化硼浆料，其原料包括氧化硼粉末、润湿分散剂一、润湿分散剂二、消泡剂、流变助剂和水；按原料总质量百分比计算：氧化硼粉末：50～60.0%；润湿分散剂一：4.0～8.0%；润湿分散剂二：1.0～2.0%；消泡剂：0.1～1.0%；流变助剂：0.3～1.5%；其余部分为水；本发明专利技术的优点在于，其氧化硼含量高，且流动性佳，同时可以较好的控制了气泡和沉淀问题，有极佳的储存稳定性。

A water-borne boron oxide slurry

The present invention discloses a water-borne boron oxide slurry, which consists of boron oxide powder, wetting dispersant one, wetting dispersant two, defoaming agent, rheological agent and water. According to the total mass percentage of raw materials, boron oxide powder is 50 to 60%; wetting dispersant is 1: 4 ~ 8%; wetting dispersant two: 1 to 2%; defoaming agent. The agent is 0.1 to 1%, the rheological agent is 0.3 to 1.5%, and the rest is water. The advantage of the invention is that the content of boron oxide is high and the fluidity is good. At the same time, it can better control the problem of bubble and precipitation, and have excellent storage stability.

【技术实现步骤摘要】
一种水性氧化硼浆料
本专利技术属于涂料
，尤其是涉及一种水性氧化硼浆料。
技术介绍
氧化硼是硼最主要的氧化物之一，可用作涂料的耐火阻燃添加剂和干燥剂，也可与多种氧化物化合制成具有特征颜色的硼玻璃、光学玻璃、耐热玻璃、仪器玻璃及玻璃纤维、光线防护材料等。目前行业使用的氧化硼浆料，氧化硼固体含量一般在45％左右，含量再做高的话，会出现粘度变大，流动性差，气泡过多，易形成硬沉淀等缺陷。给生产、储存和使用带来极大的不便。如果有一款氧化硼浆料，能做到高固含而性能稳定，那么将会节约成本、提高效率，为生产带来极大的便利。
技术实现思路
本专利技术目的是：提供一种水性氧化硼浆料，其氧化硼含量高，且流动性佳，同时可以较好的控制了气泡和沉淀问题，有极佳的储存稳定性。本专利技术的技术方案是：一种水性氧化硼浆料，其原料包括氧化硼粉末、润湿分散剂一、润湿分散剂二、消泡剂、流变助剂和水；按原料总质量百分比计算：氧化硼粉末：50.0～60.0％；润湿分散剂一：4.0～8.0％；润湿分散剂二：1.0～2.0％；消泡剂：0.1～1.0％；流变助剂：0.3～1.5％；其余部分为水。作为优选的技术方案，所述润湿分散剂一本文档来自技高网...

【技术保护点】
一种水性氧化硼浆料，其特征在于，其原料包括氧化硼粉末、润湿分散剂一、润湿分散剂二、消泡剂、流变助剂和水；按原料总质量百分比计算：氧化硼粉末：50.0～60.0%；润湿分散剂一：4.0～8.0%；润湿分散剂二：1.0～2.0%；消泡剂：0.1～1.0%；流变助剂：0.3～1.5%；其余部分为水。

【技术特征摘要】
1.一种水性氧化硼浆料，其特征在于，其原料包括氧化硼粉末、润湿分散剂一、润湿分散剂二、消泡剂、流变助剂和水；按原料总质量百分比计算：氧化硼粉末：50.0～60.0%；润湿分散剂一：4.0～8.0%；润湿分散剂二：1.0～2.0%；消泡剂：0.1～1.0%；流变助剂：0.3～1.5%；其余部分为水。2.根据权利要求1所述的水性氧化硼浆料，其特征在于，所述润湿分散剂一采用CPT可控聚合技术合成的高分子嵌段共聚物或丙烯酸酯共聚物中的至少一种。3.根据权利要求1所述的水性...