一种筷子及其生产方法技术
A kind of chopsticks and their production methods
The invention relates to the technical field of tableware manufacture, in particular to a chopstick and a production method thereof. The chopsticks include two chopsticks body, and the methods for producing chopsticks include at least the steps of mixing, granulation, injection molding, mass injection molding, grinding and packing, etc. The chopsticks produced by this method have excellent antibacterial properties, and have excellent characteristics such as acid-base resistance, high temperature resistance and chemical stability. In addition, the chopsticks can not be mouldy and can be used in various environments.
【技术实现步骤摘要】
一种筷子及其生产方法
本专利技术涉及餐具制造
，尤其涉及一种筷子及其生产方法。
技术介绍
目前市场上销售的筷子主要有竹木筷子，塑料密胺筷子及不锈钢筷子等几种。其中，竹木筷子易发霉和变质。而塑料密胺筷子在使用和高温消毒时会挥发出三聚氰胺、甲醛等有害物质，并且其化学稳定性差，容易与酸碱盐等产生反应。不锈钢筷子除医用级不锈钢外一般都含有铬镍等重金属成分，并且食用高温饭菜时，由于其导热性经常烫伤嘴部的现象。此外，目前市场上销售的这些筷子容易滋生细菌，不利于使用者的健康。
技术实现思路
针对上述存在的问题，本专利技术一方面公开了一种抗菌筷子的生产方法，所述筷子包括两根筷子本体，所述方法至少包括以下步骤：S1、搅拌：将原材料分别按重量份称重后，投料于搅拌机中进行搅拌处理，搅拌均匀后得到混合材料；其中，所述原材料包括抗菌剂和PPS塑料，所述PPS塑料的重量比为0.3-1wt％；S2、造粒：将所述混合材料加工后进行造粒处理得到原料颗粒；S3、注塑样品：开机预热注塑机并设定注塑参数，进行样品试做；若样品不合格，调整注塑参数，直至样品合格为止；S4、批量注塑：根据S3中得到合格样品...
【技术保护点】
一种生产筷子的方法，所述筷子包括两根筷子本体，其特征在于，至少包括以下步骤：S1、搅拌：将原材料分别按重量份称重后，投料于搅拌机中进行搅拌处理，搅拌均匀后得到混合材料；其中，所述原材料包括抗菌剂和PPS塑料，所述PPS塑料的重量比为0.3‑1wt％；S2、造粒：将所述混合材料加工后进行造粒处理得到原料颗粒；S3、注塑样品：开机预热注塑机并设定注塑参数，进行样品试做；若样品不合格，调整注塑参数，直至样品合格为止；S4、批量注塑：根据S3中得到合格样品的注塑参数，批量注塑生产得到产品；S5、打磨装箱：将S4中的得到的产品进行修检飞边处理后得到筷子本体，所述筷子本体经检验合格后装箱。
【技术特征摘要】
1.一种生产筷子的方法，所述筷子包括两根筷子本体，其特征在于，至少包括以下步骤：S1、搅拌：将原材料分别按重量份称重后，投料于搅拌机中进行搅拌处理，搅拌均匀后得到混合材料；其中，所述原材料包括抗菌剂和PPS塑料，所述PPS塑料的重量比为0.3-1wt％；S2、造粒：将所述混合材料加工后进行造粒处理得到原料颗粒；S3、注塑样品：开机预热注塑机并设定注塑参数，进行样品试做；若样品不合格，调整注塑参数，直至样品合格为止；S4、批量注塑：根据S3中得到合格样品的注塑参数，批量注塑生产得到产品；S5、打磨装箱：将S4中的得到的产品进行修检飞边处理后得到筷子本体，所述筷子本体经检验合格后装箱。2.根据权利要求1所述的方法，其特征在于，在S1中，所述搅拌机的参数条件为：500转/分正反转循环运行2分钟；700转/分反循环运行1...
【专利技术属性】
技术研发人员：雷刚，
申请(专利权)人：赛巴蒂奥智能家居家装江苏有限公司，
类型：发明
国别省市：江苏,32