The present invention discloses a slow release liquid coating agent compound fertilizer and its preparation method, in which the coating agent in the coating agent compound fertilizer is wrapped in the fertilizer in vitro; the coating agent includes 10 ethyl acetate 20, 10 water, 20 water, 10 polyethylene 20, 1 starch 3, 2 glycerin, 2 copies of carbon. Calcium acid 0.5, pore agent 0.5, 1, 1 lubricants, 2 animal lubricants, 5 animal oil 8, and 3 bentonite, and 3 portions of bentonite, including 500 water of water, cabbage root 30 80, sugarcane peel, corn straw, weed, animal excrement, and fulvic acid 5 and EM had 0.5 beneficial bacteria groups, 1. The fertilizer provided by the invention has been added to the rhizome of the broccoli, the sugarcane skin, the corn Platycodon and the weeds in the body. The waste is turned into a treasure, the cost is low and the preparation process is simple, at the same time, the quality of the fertilizer is improved, the release time of the fertilizer body can be extended, the number of fertilizer recovery and the artificial cost are reduced.
【技术实现步骤摘要】
一种缓释型液态包膜剂复合肥料及其制备方法
本专利技术属于包膜剂缓释肥料
,特别涉及一种缓释型液态包膜剂复合肥料及其制备方法。
技术介绍
现如今的种植生产中,为了防治植物的病虫害,为了产品的增产增收,随着化肥的大量使用,化肥的使用量大大增加,但是肥料自身的利用率不断降低,随着灌溉而溶于水中,不被植物所利用。这说明,仅靠大量增施化肥来提高作物产量是有限的,并且会污染环境,植物成熟后附带有化学肥料等,影响植物的自身质量,更甚会影响人们的健康。为此我们一直在努力探索,如何才能提高化肥利用率达到平衡施肥、合理施肥以克服其弊端的途径。现有技术中将肥料直接施加于土壤中,或者喷洒于植物叶片上等,然而当肥料直接施加于土壤中,一部分会被植物利用,另一部分则会跟随灌溉水随意流动,最终没有被植物所利用,同时污染了环境。肥料未被利用,则会增加肥料的施加量或者施加次数,造成肥料的浪费和种植成本的增加,土壤环境的恶化,增加人员的工作量。日常生活中,由于西兰花的售价贵,菜贩在出售西兰花时,每个西兰花都会带有一个很长的根茎,实质上根茎中带有一定的纤维,不能直接食用,与花菜类比,西兰花出售时带有的根茎比花菜的长太多。实质上,带有较长根茎只为了增加出售时的重量。现将西兰花的根茎作为肥料的原料,变废为宝。
技术实现思路
本专利技术提供了一种缓释型液态包膜剂复合肥料及其制备方法,以解决现有技术中肥料利用率低的问题。为了实现上述目的,本专利技术采用以下技术方案:一种缓释型液态包膜剂复合肥料,包括包膜剂和肥料本体,所述包膜剂包裹于肥料本体外;所述包膜剂按照质量份数包括:乙酸乙酯10-20份、水10- ...
【技术保护点】
一种缓释型液态包膜剂复合肥料,其特征在于:包括包膜剂和肥料本体,所述包膜剂包裹于肥料本体外;所述包膜剂按照质量份数包括:乙酸乙酯10‑20份、水10‑20份、聚乙烯10‑20份、淀粉1‑3份、甘油0.5‑2份、碳酸钙0.5‑0.8份、润滑剂1‑2份、动物油5‑8份、膨润土1‑3份;所述肥料本体按照质量份数包括:水500‑600份、西兰花根30‑80份、甘蔗皮20‑50份、玉米秸秆50‑100份、杂草50‑100份、动物粪便300‑350份、黄腐酸1‑5份和EM 有益菌群0.5‑1份。
【技术特征摘要】
1.一种缓释型液态包膜剂复合肥料,其特征在于:包括包膜剂和肥料本体,所述包膜剂包裹于肥料本体外;所述包膜剂按照质量份数包括:乙酸乙酯10-20份、水10-20份、聚乙烯10-20份、淀粉1-3份、甘油0.5-2份、碳酸钙0.5-0.8份、润滑剂1-2份、动物油5-8份、膨润土1-3份;所述肥料本体按照质量份数包括:水500-600份、西兰花根30-80份、甘蔗皮20-50份、玉米秸秆50-100份、杂草50-100份、动物粪便300-350份、黄腐酸1-5份和EM有益菌群0.5-1份。2.根据权利要求1所述的缓释型液态包膜剂复合肥料,其特征在于:所述动物油包括牛油、猪油、鸡油中的一种或多种的混合物。3.根据权利要求1所述的缓释型液态包膜剂复合肥料,其特征在于:所述包膜剂与肥料本体的质量份数比为1:30-50。4.根据权利要求1所述的缓释型液态包膜剂复合肥料,其特征在于:所述包膜剂后的肥料本体的直径为5-8mm。5.根据权利要求1-4任一所述的缓释型液态包膜剂复合肥料的制备方法,其特征在于,包括以下步骤:步骤A、将西兰花根粉碎至800-1200目,将其放于水中,在65-70℃煮30-90min,然后搅拌1-2h,过滤收集滤液,将滤渣再放于水中,在65-70℃煮30-90min,然后搅拌1-2h,过滤收集滤液,将两次滤液合并待用;步骤B、将甘蔗皮粉碎至1000-1500目,将其放于水中,在70-75℃煮60-120min,然后搅拌1-2h,过滤收集滤液,将滤渣再放于水中,在70-75℃煮60-120min,然后搅拌1-2h,过滤收集滤液,将两次滤液合并待用;步骤C、将玉米秸秆粉碎至1000-1200目,将其放于水中,在60-65℃煮30-90min,然后搅拌1-2h,过滤收集滤液,将滤渣再放于水中,在...