The invention discloses an aluminosilicate glass and a preparation method thereof, and a touch screen glass cover plate. For aluminosilicate glass, it is expressed as the mass percentage of oxide based on the oxide, containing: SiO2 57, 66%, Al2O3 12, 1, 7%; Na2O 8 8 15%; ZnO is greater than 0 and less than 4%; and ZrO2 is greater than 0 and less than 2%. The mechanical properties such as the modulus of elasticity and hardness of the cover glass can be improved through the inclusion of ZnO and ZrO2 in the glass composition, and the effect of ion exchange can be enhanced and the production cost can be reduced.
【技术实现步骤摘要】
铝硅酸盐玻璃及其制备方法、触摸屏玻璃盖板
本专利技术涉及玻璃制造领域，具体地，涉及一种铝硅酸盐玻璃，以及铝硅酸盐玻璃的制备方法，还进一步涉及一种触摸屏玻璃盖板。
技术介绍
随着世界高科技产业的不断发展，国际市场对超薄玻璃的需求正日益上升,尤其是保护平板显示器和手机用超薄玻璃盖板。平板显示器要求重量轻、体积小、便于携带，这就要求盖板玻璃的厚度必须在1mm以下。这种超薄盖板玻璃通常采用化学钢化方法使得玻璃表面进行离子交换，来增加玻璃表面压应力和压应力层深度，提高玻璃强度。同时，中心拉伸应力也会增大，这会大大增加超薄玻璃片的自爆几率。玻璃原片缺陷，钢化设备架子应力，钢化时间过长或者温度过高等任何降低玻璃强度的负面因素都可能是造成玻璃片自爆的直接原因。超薄玻璃片发生自爆碎片的深层次原因是超薄玻璃的杨氏模量、抗折强度、表面硬度等力学性能偏弱，这给超薄玻璃的实际应用带来了巨大的阻碍。玻璃块经线切割机切割成厚度0.3-1.1mm的薄片，再经研磨和抛光后，将薄玻璃片置于硝酸钾化学钢化液中进行强化处理，在化学钢化过程中，玻璃片可能会发生自爆碎成小片，大大降低了钢化玻璃的成品率，从而...
【技术保护点】
一种铝硅酸盐玻璃，以氧化物为基准的质量百分比表示，含有：SiO2：57‑66％；Al2O3：12‑23％；MgO：1‑7％；Na2O：8‑15％；ZnO：大于0且小于等于4％；ZrO2：大于0且小于等于2％。
【技术特征摘要】
1.一种铝硅酸盐玻璃，以氧化物为基准的质量百分比表示，含有：SiO2：57-66％；Al2O3：12-23％；MgO：1-7％；Na2O：8-15％；ZnO：大于0且小于等于4％；ZrO2：大于0且小于等于2％。2.根据权利要求1所述的铝硅酸盐玻璃，其特征在于，以氧化物为基准的质量百分比表示，还包括B2O30-8％，并且0.15≤(ZrO2+ZnO+B2O3)/Al2O3≤0.37。3.根据权利要求1所述的铝硅酸盐玻璃，其特征在于，以氧化物为基准的质量百分比表示，还包括K2O0.5-6.5％，10≤Na2O+K2O≤17。4.根据权利要求1所述的铝硅酸盐玻璃，其特征在于，以氧化物为基准的质量百分比表示，所述ZnO的含量为0＜ZnO≤4。5.根据权利要求4所述的铝硅酸盐玻璃，其特征在于，以氧化物为基准的质量百分比表示，所述ZnO的含量为0.5≤ZnO≤2。6.根据权利要求1所述的铝硅酸盐玻璃，其特征在于，以氧化物为基准的质量百分比表示，所述ZrO2的含量为0＜ZrO2≤2。7.根据权利要求6所述的铝硅酸盐玻璃，其特征在于，以氧化物为基准的质量百分比表示，所述ZrO2的含量为0.5≤ZnO≤...
【专利技术属性】
技术研发人员：刘攀，肖子凡，邓臻禄，戴斌，何浩波，
申请(专利权)人：中国南玻集团股份有限公司，深圳南玻应用技术有限公司，
类型：发明
国别省市：广东,44